Fiscal 1997 survey report. Subtask 6 (hydrogen utilization worldwide clean energy system technology) (WE-NET) (development of technology of low temperature materials); 1997 nendo seika hokokusho. Suiso riyo kokusai clean energy system gijutsu (WE-NET) subtask 6 teion zairyo gijutsu no kaihatsu

Abstract

The paper described the results of the development of technology of low temperature materials in the fiscal 1997 WE-NET. Using experimental equipment for materials under the atmosphere of liquid hydrogen, an experiment on mechanical characteristics under the liquid hydrogen atmosphere (20K) was conducted of the base materials of candidate steels (SUS304L, SUS316L and A5083). In material evaluation experiments (tension/fracture toughness/fracture tests), characteristic behaviors of the materials were shown which are different from those shown in the environment of liquid He (4k), etc. Even if the amount of {delta} ferrite in the metal welded of the stainless steel is small, approximately 1%, the degradation of low temperature toughness occurred. Welded joints of stainless steel by submerged arc welding and MAG welding were in now way inferior in tension characteristic to those by TIG welding, but were inferior in toughness ranging from room temperature to extremely low temperature. As to aluminum alloys, materials excellent in extremely-low temperature toughness were able to be found. Under the low temperature hydrogen gas atmosphere, the lower the strain rate is, the higher the hydrogen brittleness susceptibility is around 220K (extremely large hydrogen brittleness temperature) (SUS304L). In the hydrogen gas of 100 atm, hydrogen invades the material  More>>
Authors:
"NONE"
Publication Date:
Mar 01, 1998
Product Type:
Technical Report
Report Number:
NEDO-WE-NET-976
Reference Number:
SCA: 420500; 360103; 080000; PA: JP-98:0B0364; EDB-99:063715; SN: 99002080869
Resource Relation:
Other Information: PBD: Mar 1998
Subject:
42 ENGINEERING NOT INCLUDED IN OTHER CATEGORIES; 36 MATERIALS SCIENCE; 08 HYDROGEN FUEL; HYDROGEN-BASED ECONOMY; GLOBAL ASPECTS; INTERNATIONAL COOPERATION; MATERIALS; ENERGY SYSTEMS; POLLUTION ABATEMENT; CRYOGENICS; MECHANICAL PROPERTIES; LIQUEFIED GASES; HYDROGEN; STAINLESS STEEL-304L; STAINLESS STEEL-316L; ALUMINIUM ALLOYS; MATRIX MATERIALS; WELDING; FRACTURE PROPERTIES; HYDROGEN EMBRITTLEMENT
OSTI ID:
350802
Research Organizations:
New Energy and Industrial Technology Development Organization, Tokyo (Japan)
Country of Origin:
Japan
Language:
Japanese
Other Identifying Numbers:
Other: ON: DE99736783; TRN: JN98B0364
Availability:
OSTI as DE99736783
Submitting Site:
NEDO
Size:
334 p.
Announcement Date:

Citation Formats

Fiscal 1997 survey report. Subtask 6 (hydrogen utilization worldwide clean energy system technology) (WE-NET) (development of technology of low temperature materials); 1997 nendo seika hokokusho. Suiso riyo kokusai clean energy system gijutsu (WE-NET) subtask 6 teion zairyo gijutsu no kaihatsu. Japan: N. p., 1998. Web.
Fiscal 1997 survey report. Subtask 6 (hydrogen utilization worldwide clean energy system technology) (WE-NET) (development of technology of low temperature materials); 1997 nendo seika hokokusho. Suiso riyo kokusai clean energy system gijutsu (WE-NET) subtask 6 teion zairyo gijutsu no kaihatsu. Japan.
1998. "Fiscal 1997 survey report. Subtask 6 (hydrogen utilization worldwide clean energy system technology) (WE-NET) (development of technology of low temperature materials); 1997 nendo seika hokokusho. Suiso riyo kokusai clean energy system gijutsu (WE-NET) subtask 6 teion zairyo gijutsu no kaihatsu." Japan.
@misc{etde_350802,
title = {Fiscal 1997 survey report. Subtask 6 (hydrogen utilization worldwide clean energy system technology) (WE-NET) (development of technology of low temperature materials); 1997 nendo seika hokokusho. Suiso riyo kokusai clean energy system gijutsu (WE-NET) subtask 6 teion zairyo gijutsu no kaihatsu}
abstractNote = {The paper described the results of the development of technology of low temperature materials in the fiscal 1997 WE-NET. Using experimental equipment for materials under the atmosphere of liquid hydrogen, an experiment on mechanical characteristics under the liquid hydrogen atmosphere (20K) was conducted of the base materials of candidate steels (SUS304L, SUS316L and A5083). In material evaluation experiments (tension/fracture toughness/fracture tests), characteristic behaviors of the materials were shown which are different from those shown in the environment of liquid He (4k), etc. Even if the amount of {delta} ferrite in the metal welded of the stainless steel is small, approximately 1%, the degradation of low temperature toughness occurred. Welded joints of stainless steel by submerged arc welding and MAG welding were in now way inferior in tension characteristic to those by TIG welding, but were inferior in toughness ranging from room temperature to extremely low temperature. As to aluminum alloys, materials excellent in extremely-low temperature toughness were able to be found. Under the low temperature hydrogen gas atmosphere, the lower the strain rate is, the higher the hydrogen brittleness susceptibility is around 220K (extremely large hydrogen brittleness temperature) (SUS304L). In the hydrogen gas of 100 atm, hydrogen invades the material at 100degC, but does not at 77k. 38 refs., 173 figs., 48 tabs.}
place = {Japan}
year = {1998}
month = {Mar}
}