A range of critical experiments has been performed studying the creep and fracture behaviour of a typical CrMoV rotor steel. Initially, uniaxial tests were carried out to provide material with a predetermined level of creep damage. Then, miniature disc tests were undertaken under accelerated conditions in a similar manner to procedures used for post-exposure uniaxial testing of service components. Data analysis demonstrates that the miniature tests accurately reflect the damage present so that this approach can be used to support run/repair/replace decisions. (orig.) 8 refs.