Abstract
In order to better understand the mechanisms involved in Alloy 600`s stress corrosion cracking in PWR environment, laboratory tests were performed. The influence of parameters pertinent to the mechanisms was studies : hydrogen and oxygen overpressures, local chemical composition, microstructure. The results show that neither hydrogen nor dissolution/oxidation, despite their respective roles in the process, are sufficient to account for experimental facts. SEM observation of micro-cleavage facets on specimens` fracture surfaces leads to pay attention to a new mechanism of corrosion/plasticity interactions. (author). 113 refs., 73 figs., 15 tabs., 4 annexes.
Citation Formats
Rios, R.
Study of alloy 600`S stress corrosion cracking mechanisms in high temperature water; Etude des mecanismes de corrosion sous contrainte de l`alliage 600 dans l`eau a haute temperature.
France: N. p.,
1994.
Web.
Rios, R.
Study of alloy 600`S stress corrosion cracking mechanisms in high temperature water; Etude des mecanismes de corrosion sous contrainte de l`alliage 600 dans l`eau a haute temperature.
France.
Rios, R.
1994.
"Study of alloy 600`S stress corrosion cracking mechanisms in high temperature water; Etude des mecanismes de corrosion sous contrainte de l`alliage 600 dans l`eau a haute temperature."
France.
@misc{etde_246800,
title = {Study of alloy 600`S stress corrosion cracking mechanisms in high temperature water; Etude des mecanismes de corrosion sous contrainte de l`alliage 600 dans l`eau a haute temperature}
author = {Rios, R}
abstractNote = {In order to better understand the mechanisms involved in Alloy 600`s stress corrosion cracking in PWR environment, laboratory tests were performed. The influence of parameters pertinent to the mechanisms was studies : hydrogen and oxygen overpressures, local chemical composition, microstructure. The results show that neither hydrogen nor dissolution/oxidation, despite their respective roles in the process, are sufficient to account for experimental facts. SEM observation of micro-cleavage facets on specimens` fracture surfaces leads to pay attention to a new mechanism of corrosion/plasticity interactions. (author). 113 refs., 73 figs., 15 tabs., 4 annexes.}
place = {France}
year = {1994}
month = {Jun}
}
title = {Study of alloy 600`S stress corrosion cracking mechanisms in high temperature water; Etude des mecanismes de corrosion sous contrainte de l`alliage 600 dans l`eau a haute temperature}
author = {Rios, R}
abstractNote = {In order to better understand the mechanisms involved in Alloy 600`s stress corrosion cracking in PWR environment, laboratory tests were performed. The influence of parameters pertinent to the mechanisms was studies : hydrogen and oxygen overpressures, local chemical composition, microstructure. The results show that neither hydrogen nor dissolution/oxidation, despite their respective roles in the process, are sufficient to account for experimental facts. SEM observation of micro-cleavage facets on specimens` fracture surfaces leads to pay attention to a new mechanism of corrosion/plasticity interactions. (author). 113 refs., 73 figs., 15 tabs., 4 annexes.}
place = {France}
year = {1994}
month = {Jun}
}