Comparison of Irradiation Damage in Artificial and Natural Graphite at Different Irradiation Temperatures; Comparaison des dommages subis par des graphites artificiels et naturels irradiés a des températures différentes; СРАВНЕНИЕ РАДИАЦИОННЫХ ПОВРЕЖДЕНИЙ В ИСКУССТВЕННОМ И ПРИРОДНОМ ГРАФИТЕ ПРИ РАЗЛИЧНЫХ ТЕМПЕРАТУРАХ ВО ВРЕМЯ ОБЛУЧЕНИЯ; Comparación entre los danos causados por las radiaciones en grafitos artificiales y naturales por irradiacion a diversas temperaturas

Abstract

Results of irradiation experiments on artificial and natural graphite in the three temperature ranges 70 - 150°C, 300 - 400°C and 550 - 650°C are compared. These irradiation experiments were carried out in core or pool positions of the GETR, Vallecitos. The samples investigated received neutron doses up to 5 x l0{sup 21} nvt with E > 0.17 eV, which is approximately 3 x l0{sup 21} nvt with E > 0.18 MeV. Changes in the lattice parameters, the electric and thermal conductivity, the macroscopic dimensions and the bending strength are discussed. The natural graphite samples investigated were manufactured partly with, partly without a binding material. The results obtained during these investigations indicate, in addition to the dependence on the irradiation temperature and the neutron dose, a strong influence exerted by the basic materials, the treatment during production and the density. Strong anisotropic effects in natural graphite at lower irradiation temperatures, resulting from the treatment during production, level out at higher irradiation temperatures. (author) [French] L'auteur compare les résultats d'expériences consistant à exposer du graphite artificiel et naturel à un flux de neutrons, à des températures comprises dans les trois gammes suivantes: 70 - 150°C, 300 - 400°C et 550 -  More>>
Authors:
Gain, R. [1] 
  1. Reactor Materials Institute, Jülich Nuclear Research Establishment, Jülich, Federal Republic of Germany (Germany)
Publication Date:
Aug 15, 1963
Product Type:
Conference
Resource Relation:
Conference: Symposium on Radiation Damage in Solids and Reactor Materials, Venice (Italy), 7-11 May 1962; Other Information: 11 refs., 10 figs., 1 tab.; Related Information: In: Radiation Damage in Reactor Materials. Part of the Proceedings of the Symposium on Radiation Damage in Solids and Reactor Materials| 773 p.
Subject:
36 MATERIALS SCIENCE; 22 GENERAL STUDIES OF NUCLEAR REACTORS; ANISOTROPY; DENSITY; EV RANGE; FLEXURAL STRENGTH; GENETIC RADIATION EFFECTS; GRAPHITE; IRRADIATION; LATTICE PARAMETERS; MEV RANGE; NEUTRONS; RADIATION DOSES; TEMPERATURE RANGE 0273-0400 K; THERMAL CONDUCTIVITY
OSTI ID:
22334324
Research Organizations:
International Atomic Energy Agency, Vienna (Austria)
Country of Origin:
IAEA
Language:
English
Other Identifying Numbers:
Other: ISSN 0074-1884; TRN: XA15M0309040608
Submitting Site:
INIS
Size:
page(s) 651-662
Announcement Date:
May 12, 2015

Citation Formats

Gain, R. Comparison of Irradiation Damage in Artificial and Natural Graphite at Different Irradiation Temperatures; Comparaison des dommages subis par des graphites artificiels et naturels irradiés a des températures différentes; СРАВНЕНИЕ РАДИАЦИОННЫХ ПОВРЕЖДЕНИЙ В ИСКУССТВЕННОМ И ПРИРОДНОМ ГРАФИТЕ ПРИ РАЗЛИЧНЫХ ТЕМПЕРАТУРАХ ВО ВРЕМЯ ОБЛУЧЕНИЯ; Comparación entre los danos causados por las radiaciones en grafitos artificiales y naturales por irradiacion a diversas temperaturas. IAEA: N. p., 1963. Web.
Gain, R. Comparison of Irradiation Damage in Artificial and Natural Graphite at Different Irradiation Temperatures; Comparaison des dommages subis par des graphites artificiels et naturels irradiés a des températures différentes; СРАВНЕНИЕ РАДИАЦИОННЫХ ПОВРЕЖДЕНИЙ В ИСКУССТВЕННОМ И ПРИРОДНОМ ГРАФИТЕ ПРИ РАЗЛИЧНЫХ ТЕМПЕРАТУРАХ ВО ВРЕМЯ ОБЛУЧЕНИЯ; Comparación entre los danos causados por las radiaciones en grafitos artificiales y naturales por irradiacion a diversas temperaturas. IAEA.
Gain, R. 1963. "Comparison of Irradiation Damage in Artificial and Natural Graphite at Different Irradiation Temperatures; Comparaison des dommages subis par des graphites artificiels et naturels irradiés a des températures différentes; СРАВНЕНИЕ РАДИАЦИОННЫХ ПОВРЕЖДЕНИЙ В ИСКУССТВЕННОМ И ПРИРОДНОМ ГРАФИТЕ ПРИ РАЗЛИЧНЫХ ТЕМПЕРАТУРАХ ВО ВРЕМЯ ОБЛУЧЕНИЯ; Comparación entre los danos causados por las radiaciones en grafitos artificiales y naturales por irradiacion a diversas temperaturas." IAEA.
@misc{etde_22334324,
title = {Comparison of Irradiation Damage in Artificial and Natural Graphite at Different Irradiation Temperatures; Comparaison des dommages subis par des graphites artificiels et naturels irradiés a des températures différentes; СРАВНЕНИЕ РАДИАЦИОННЫХ ПОВРЕЖДЕНИЙ В ИСКУССТВЕННОМ И ПРИРОДНОМ ГРАФИТЕ ПРИ РАЗЛИЧНЫХ ТЕМПЕРАТУРАХ ВО ВРЕМЯ ОБЛУЧЕНИЯ; Comparación entre los danos causados por las radiaciones en grafitos artificiales y naturales por irradiacion a diversas temperaturas}
author = {Gain, R.}
abstractNote = {Results of irradiation experiments on artificial and natural graphite in the three temperature ranges 70 - 150°C, 300 - 400°C and 550 - 650°C are compared. These irradiation experiments were carried out in core or pool positions of the GETR, Vallecitos. The samples investigated received neutron doses up to 5 x l0{sup 21} nvt with E > 0.17 eV, which is approximately 3 x l0{sup 21} nvt with E > 0.18 MeV. Changes in the lattice parameters, the electric and thermal conductivity, the macroscopic dimensions and the bending strength are discussed. The natural graphite samples investigated were manufactured partly with, partly without a binding material. The results obtained during these investigations indicate, in addition to the dependence on the irradiation temperature and the neutron dose, a strong influence exerted by the basic materials, the treatment during production and the density. Strong anisotropic effects in natural graphite at lower irradiation temperatures, resulting from the treatment during production, level out at higher irradiation temperatures. (author) [French] L'auteur compare les résultats d'expériences consistant à exposer du graphite artificiel et naturel à un flux de neutrons, à des températures comprises dans les trois gammes suivantes: 70 - 150°C, 300 - 400°C et 550 - 650°C. Ces expériences ont eu lieu tant à 1'intérieur qu’à I'extérieur du coeur du réacteur GETR de Vallecitos. Les échantillons étudiés ont reçu des doses allant jusqu'à 5 * 10{sup 21} nvt avec une énergie de E > 0,17 eV, ce qui correspond à environ 3 * 10{sup 21} nvt avec E> 0,18 MeV. L’autei» discute les modifications observées dans les paramètres de réseau, la conductivité électrique et thermique, les dimensions macroscopiques et la flexibilité. Les échantillons de graphite naturel considérés avaient été fabriqués en partie à l'aide d'une substance liante et en partie sans une telle substance. Il ressort de ces expériences que les résultats varient non seulement avec la température d'irradiation et la dose de neutrons mais qu'ils sont déterminés dans une forte mesure par les matériaux de base, le traitement au cours de la fabrication et la densité. Les effets anisotropiques considérables qu'on observe dans le graphite naturel à des températures d’irradiation relativement peu élevées et qui résultent du traitement au cours de la fabrication, s'atténuent graduellement lorsque la température d'irradiation augmente. (author) [Spanish] La memoria compara los resultados de experimentos de irradiaciún de grafito artificial y natural en tres intervalos de temperatura que abarcan de 70 - 150°C, de 300 - 400°C y de 550 - 650°C, respectivamente. Los experimentos se efectuaron en el cuerpo o en el tanque del reactor GETR de Vallecitos. Las muestras investigadas recibieron dosis neutrónicas de hasta 5 • 10{sup 21} nvt, con E > 0,17 eV, lo que corresponde aproximadamente a 3 • 10{sup 21} nvt, con E > 0,18 MeV. La memoria discute las alteraciones sufridas por los parámetros de la red cristalina, la conductividad eléctrica y térmica, las dimensiones macroscópicas y la resistencia a la ilexion. Las muestras de grafito natural investigadas fueron preparadas en parte con material aglomerante y en parte sin él. Los resultados obtenidos durante estas investigaciones indican que. además de la temperatura de irradiación y de la dosis neuttónica, las materias primas, el tratamiento recibido durante la elaljoración y la densidad ejercen una influencia muy marcada. Los tuertes efectos anisotrópicos que aparecen en el grafito natural a reducidas temperaturas de irradiación, y que son resultado del tratamiento durante la elaboración.quedan compensados al irradiar a temperaturas más elevadas. (author) [Russian] Сравниваются результаты опытов облучения искуственного и природного графита при температурах в пределах от 70 до 150°С, от 300 до 400°С и от 550 до 650°С. Опыты производились в активной зоне или в бассейне реактора GETR в Вальлеситосе. Обследованные образцы были подвергнуты воздействию доз нейтронов до 5 • 10{sup 21} nvt при Е > 0,17 Мэв, что соответствует приблизительно 3 * 10{sup 21} nvt при Е > 0,16 Мэв. Обсуждаются изменения параметров решетки, электропроводимости и теплопроводности, микроскопических размеров и сопротивления на изгиб. Изученные образцы природного графита были изготовлены частью со связующим материалом, а частью без него. Полученные при этих исследованиях результаты показывают, что, помимо зависимости от температуры при облучении и от дозы нейтронов, имеет место также сильная зависимость от исходных материалов, обработки во время изготовления и плотности. Сильное анизотропное воздействие в природном графите при более низких температурах во время облучения, возникающее в результате обработки в процессе производства, выравнивается при облучении при более высоких температурах. (author)}
place = {IAEA}
year = {1963}
month = {Aug}
}