The corrosion behavior of gas metal arc welding (GMAW) regions has been studied using potentiodynamic polarization and polarization resistance (LPR) techniques. Experiments were conducted in hydrogen sulfide (H{sub 2}S)-containing brine and in H{sub 2}S-free brine. Welds were made on API 5L X52 steel. Due to differences in their microstructure, chemical composition and residual stress level, weld regions exhibited different responses under H{sub 2}S corrosion. Base metal exhibited the highest corrosion rate (CR) and the most cathodic corrosion potential. [Spanish] Se estudio el comportamiento ante la corrosion de las regiones de soldadura de un cordon realizado por arco metalico con gas (GMAW) sobre un acero grado API X52 mediante las tecnicas de polarizacion potencio dinamica y resistencia a la polarizacion (LPR). Los experimentos se realizaron utilizando salmuera con 300 ppm de acido sulfhidrico (H{sub 2}S) y salmuera libre de H{sub 2}S como electrolitos. Debido a las diferencias en su microestructura, composicion quimica y el nivel de esfuerzos residuales, las regiones de soldadura mostraron diferentes respuestas a la corrosion por H{sub 2}S. El metal base exhibio la velocidad de corrosion (VC) mas alta y el potencial de corrosion mas catodico.
Arenas-Martinez, L.F . E-mail: fernando.arenas@uadec.edu.mx;
[1]
Garcia-Cerecero, G.
[2]
- Universidad Autonoma de Coahuila, Coahuila (Mexico)
- Corporacion Mexicana de Investigacion en Materiales S.A. de C.V., Saltillo, Coahuila (Mexico)
Citation Formats
Arenas-Martinez, L.F . E-mail: fernando.arenas@uadec.edu.mx, and Garcia-Cerecero, G.
Hydrogen sulfide corrosion of weld regions in API X52 steel; Corrosion por acido sulfhidrico de las regiones de soldadura en acero API X52.
Mexico: N. p.,
2012.
Web.
Arenas-Martinez, L.F . E-mail: fernando.arenas@uadec.edu.mx, & Garcia-Cerecero, G.
Hydrogen sulfide corrosion of weld regions in API X52 steel; Corrosion por acido sulfhidrico de las regiones de soldadura en acero API X52.
Mexico.
Arenas-Martinez, L.F . E-mail: fernando.arenas@uadec.edu.mx, and Garcia-Cerecero, G.
2012.
"Hydrogen sulfide corrosion of weld regions in API X52 steel; Corrosion por acido sulfhidrico de las regiones de soldadura en acero API X52."
Mexico.
@misc{etde_22134383,
title = {Hydrogen sulfide corrosion of weld regions in API X52 steel; Corrosion por acido sulfhidrico de las regiones de soldadura en acero API X52}
author = {Arenas-Martinez, L.F . E-mail: fernando.arenas@uadec.edu.mx, and Garcia-Cerecero, G.}
abstractNote = {The corrosion behavior of gas metal arc welding (GMAW) regions has been studied using potentiodynamic polarization and polarization resistance (LPR) techniques. Experiments were conducted in hydrogen sulfide (H{sub 2}S)-containing brine and in H{sub 2}S-free brine. Welds were made on API 5L X52 steel. Due to differences in their microstructure, chemical composition and residual stress level, weld regions exhibited different responses under H{sub 2}S corrosion. Base metal exhibited the highest corrosion rate (CR) and the most cathodic corrosion potential. [Spanish] Se estudio el comportamiento ante la corrosion de las regiones de soldadura de un cordon realizado por arco metalico con gas (GMAW) sobre un acero grado API X52 mediante las tecnicas de polarizacion potencio dinamica y resistencia a la polarizacion (LPR). Los experimentos se realizaron utilizando salmuera con 300 ppm de acido sulfhidrico (H{sub 2}S) y salmuera libre de H{sub 2}S como electrolitos. Debido a las diferencias en su microestructura, composicion quimica y el nivel de esfuerzos residuales, las regiones de soldadura mostraron diferentes respuestas a la corrosion por H{sub 2}S. El metal base exhibio la velocidad de corrosion (VC) mas alta y el potencial de corrosion mas catodico.}
journal = []
issue = {4}
volume = {13}
journal type = {AC}
place = {Mexico}
year = {2012}
month = {Oct}
}
title = {Hydrogen sulfide corrosion of weld regions in API X52 steel; Corrosion por acido sulfhidrico de las regiones de soldadura en acero API X52}
author = {Arenas-Martinez, L.F . E-mail: fernando.arenas@uadec.edu.mx, and Garcia-Cerecero, G.}
abstractNote = {The corrosion behavior of gas metal arc welding (GMAW) regions has been studied using potentiodynamic polarization and polarization resistance (LPR) techniques. Experiments were conducted in hydrogen sulfide (H{sub 2}S)-containing brine and in H{sub 2}S-free brine. Welds were made on API 5L X52 steel. Due to differences in their microstructure, chemical composition and residual stress level, weld regions exhibited different responses under H{sub 2}S corrosion. Base metal exhibited the highest corrosion rate (CR) and the most cathodic corrosion potential. [Spanish] Se estudio el comportamiento ante la corrosion de las regiones de soldadura de un cordon realizado por arco metalico con gas (GMAW) sobre un acero grado API X52 mediante las tecnicas de polarizacion potencio dinamica y resistencia a la polarizacion (LPR). Los experimentos se realizaron utilizando salmuera con 300 ppm de acido sulfhidrico (H{sub 2}S) y salmuera libre de H{sub 2}S como electrolitos. Debido a las diferencias en su microestructura, composicion quimica y el nivel de esfuerzos residuales, las regiones de soldadura mostraron diferentes respuestas a la corrosion por H{sub 2}S. El metal base exhibio la velocidad de corrosion (VC) mas alta y el potencial de corrosion mas catodico.}
journal = []
issue = {4}
volume = {13}
journal type = {AC}
place = {Mexico}
year = {2012}
month = {Oct}
}