Abstract
The grafting of methacrylic acid to nylon by the preirradiation technique has been studied. The rate of grafting is appreciably larger than that of homopolymerization. No simple relation exists between reaction rate and total dose. The temperature dependence of the rate of grafting to the fibre, preirradiated in air, indicates that initiation of grafting is likely to take place by decomposition of peroxide groups formed on irradiation. Electrical resistance measurements on the irradiated fibre indicate that this has been reduced by a factor of 10. (author) [French] On a etudie le greffage de l'acide methacrylique sur du nylon par la technique de preirradiation. La vitesse du greffage est sensiblement plus grande que celle de l'homopolymerisation. Il n'existe pas de rapport simple entre la vitesse de reaction et la dose totale. Le fait que la vitesse du greffage sur la fibre, pre-irradiee a l'air, depend de la temperature, indique que l'amorcage de la greffe est susceptible d'etre provoque par la decomposition des groupements de peroxyde formes lors de l'irradiation. Les mesures de resistance electrique effectuees sur la fibre irradiee indiquent que cette resistance a ete reduite au dixieme de la valeur originale. (author) [Spanish] Al estudiar la copolimerizacio n de injerto
More>>
Citation Formats
Roberts, R, and Thomas, J K.
The Radiation Induced Graft Copolymerization of Methacrylic Acid to Nylon; Copolymerisation par greffe de l'acide methacrylique sur le nylon, provoquee par irradiation; Obluchenie vyzyvaet graft-kopolimerizats yu metakrilovoj kisloty v nejlone; Injerto del acido metacrilico en el nylon por copolimerizacion radioinducida.
IAEA: N. p.,
1960.
Web.
Roberts, R, & Thomas, J K.
The Radiation Induced Graft Copolymerization of Methacrylic Acid to Nylon; Copolymerisation par greffe de l'acide methacrylique sur le nylon, provoquee par irradiation; Obluchenie vyzyvaet graft-kopolimerizats yu metakrilovoj kisloty v nejlone; Injerto del acido metacrilico en el nylon por copolimerizacion radioinducida.
IAEA.
Roberts, R, and Thomas, J K.
1960.
"The Radiation Induced Graft Copolymerization of Methacrylic Acid to Nylon; Copolymerisation par greffe de l'acide methacrylique sur le nylon, provoquee par irradiation; Obluchenie vyzyvaet graft-kopolimerizats yu metakrilovoj kisloty v nejlone; Injerto del acido metacrilico en el nylon por copolimerizacion radioinducida."
IAEA.
@misc{etde_22025828,
title = {The Radiation Induced Graft Copolymerization of Methacrylic Acid to Nylon; Copolymerisation par greffe de l'acide methacrylique sur le nylon, provoquee par irradiation; Obluchenie vyzyvaet graft-kopolimerizats yu metakrilovoj kisloty v nejlone; Injerto del acido metacrilico en el nylon por copolimerizacion radioinducida}
author = {Roberts, R, and Thomas, J K}
abstractNote = {The grafting of methacrylic acid to nylon by the preirradiation technique has been studied. The rate of grafting is appreciably larger than that of homopolymerization. No simple relation exists between reaction rate and total dose. The temperature dependence of the rate of grafting to the fibre, preirradiated in air, indicates that initiation of grafting is likely to take place by decomposition of peroxide groups formed on irradiation. Electrical resistance measurements on the irradiated fibre indicate that this has been reduced by a factor of 10. (author) [French] On a etudie le greffage de l'acide methacrylique sur du nylon par la technique de preirradiation. La vitesse du greffage est sensiblement plus grande que celle de l'homopolymerisation. Il n'existe pas de rapport simple entre la vitesse de reaction et la dose totale. Le fait que la vitesse du greffage sur la fibre, pre-irradiee a l'air, depend de la temperature, indique que l'amorcage de la greffe est susceptible d'etre provoque par la decomposition des groupements de peroxyde formes lors de l'irradiation. Les mesures de resistance electrique effectuees sur la fibre irradiee indiquent que cette resistance a ete reduite au dixieme de la valeur originale. (author) [Spanish] Al estudiar la copolimerizacio n de injerto del acido metacrilico en el nylon por el procedimiento de preirradiacion, los autores comprobaron que la velocidad de injerto es sensiblemente mas elevada que la de homopolimerizacion. No existe una relacion sencilla entre la velocidad de reaccion y la dosis total. La influencia de la temperatura sobre la velocidad de injerto en la fibra previamente irradiada en aire indica que el proceso se inicia por descomposicion de los grupos peroxido formados durante la irradiacion. Las mediciones efectuadas demuestran que la resistencia electrica de la fibra irradiada solo alcanza la decima parte de la correspondiente a la fibra no tratada. (author) [Russian] Bylo provedeno izuchenie prosachivaniya metakrilovoj kisloty v nejlon putem podgotovki k oblucheniyu. Skorost' prosachivaniya otnositel'no bol'she, chem skorost' komopolimerizatsii. Ne sushchestvuet prostoj svyazi mezhdu skorost'yu reaktsii i vsej dozoj. Temperaturnaya zavisimost' skorosti prosachivaniya v volokno, podgotovlennoe k oblucheniyu v vozdukhe, ukazyvaet, chto nachalo prosachivaniya, po-vidimomu, proiskhodit putem razlozheniya peroksidnykh grupp, obrazovannykh posle oblucheniya. Izmereniya ehlektricheskogo soprotivleniya na obluchennom volokne ukazyvayut, chto razlozhenie umen'shaetsya na koehffitsient 10. (author)}
place = {IAEA}
year = {1960}
month = {Jul}
}
title = {The Radiation Induced Graft Copolymerization of Methacrylic Acid to Nylon; Copolymerisation par greffe de l'acide methacrylique sur le nylon, provoquee par irradiation; Obluchenie vyzyvaet graft-kopolimerizats yu metakrilovoj kisloty v nejlone; Injerto del acido metacrilico en el nylon por copolimerizacion radioinducida}
author = {Roberts, R, and Thomas, J K}
abstractNote = {The grafting of methacrylic acid to nylon by the preirradiation technique has been studied. The rate of grafting is appreciably larger than that of homopolymerization. No simple relation exists between reaction rate and total dose. The temperature dependence of the rate of grafting to the fibre, preirradiated in air, indicates that initiation of grafting is likely to take place by decomposition of peroxide groups formed on irradiation. Electrical resistance measurements on the irradiated fibre indicate that this has been reduced by a factor of 10. (author) [French] On a etudie le greffage de l'acide methacrylique sur du nylon par la technique de preirradiation. La vitesse du greffage est sensiblement plus grande que celle de l'homopolymerisation. Il n'existe pas de rapport simple entre la vitesse de reaction et la dose totale. Le fait que la vitesse du greffage sur la fibre, pre-irradiee a l'air, depend de la temperature, indique que l'amorcage de la greffe est susceptible d'etre provoque par la decomposition des groupements de peroxyde formes lors de l'irradiation. Les mesures de resistance electrique effectuees sur la fibre irradiee indiquent que cette resistance a ete reduite au dixieme de la valeur originale. (author) [Spanish] Al estudiar la copolimerizacio n de injerto del acido metacrilico en el nylon por el procedimiento de preirradiacion, los autores comprobaron que la velocidad de injerto es sensiblemente mas elevada que la de homopolimerizacion. No existe una relacion sencilla entre la velocidad de reaccion y la dosis total. La influencia de la temperatura sobre la velocidad de injerto en la fibra previamente irradiada en aire indica que el proceso se inicia por descomposicion de los grupos peroxido formados durante la irradiacion. Las mediciones efectuadas demuestran que la resistencia electrica de la fibra irradiada solo alcanza la decima parte de la correspondiente a la fibra no tratada. (author) [Russian] Bylo provedeno izuchenie prosachivaniya metakrilovoj kisloty v nejlon putem podgotovki k oblucheniyu. Skorost' prosachivaniya otnositel'no bol'she, chem skorost' komopolimerizatsii. Ne sushchestvuet prostoj svyazi mezhdu skorost'yu reaktsii i vsej dozoj. Temperaturnaya zavisimost' skorosti prosachivaniya v volokno, podgotovlennoe k oblucheniyu v vozdukhe, ukazyvaet, chto nachalo prosachivaniya, po-vidimomu, proiskhodit putem razlozheniya peroksidnykh grupp, obrazovannykh posle oblucheniya. Izmereniya ehlektricheskogo soprotivleniya na obluchennom volokne ukazyvayut, chto razlozhenie umen'shaetsya na koehffitsient 10. (author)}
place = {IAEA}
year = {1960}
month = {Jul}
}