Oxygen permeation and thermo-chemical stability of oxygen separation membrane materials for the oxyfuel process

Abstract

The reduction of CO{sub 2} emissions, generally held to be one of the most significant contributors to global warming, is a major technological issue. CO{sub 2} Capture and Storage (CCS) techniques applied to large stationary sources such as coal-fired power plants could efficiently contribute to the global carbon mitigation effort. The oxyfuel process, which consists in the burning of coal in an oxygen-rich atmosphere to produce a flue gas highly concentrated in CO{sub 2}, is a technology considered for zero CO{sub 2} emission coal-fired power plants. The production of this O{sub 2}-rich combustion gas from air can be carried out using high purity oxygen separation membranes. Some of the most promising materials for this application are mixed ionic-electronic conducting (MIEC) materials with perovskite and K{sub 2}NiF{sub 4} perovskite-related structures. The present work examines the selection of La{sub 0.58}Sr{sub 0.4}Co{sub 0.2}Fe{sub 0.8}O{sub 3-{delta}} (LSCF58), La{sub 2}NiO{sub 4+{delta}}, Pr{sub 0.58}Sr{sub 0.4}Co{sub 0.2}Fe{sub 0.8}O{sub 3-{delta}} (PSCF58) and Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-{delta}} (BSCF50) as membrane materials for the separation of O{sub 2} and N{sub 2} in the framework of the oxyfuel process with flue gas recycling. Annealing experiments were carried out on pellets exposed to CO{sub 2}, water vapour, O{sub 2} and  More>>
Publication Date:
Jul 01, 2009
Product Type:
Thesis/Dissertation
Report Number:
ETDE-DE-2416
Resource Relation:
Other Information: TH: Diss.; Related Information: Schriften des Forschungszentrums Juelich. Reihe Energie und Umwelt/Energy and Environmentv. 43
Subject:
36 MATERIALS SCIENCE; MEMBRANES; OXYFUEL COMBUSTION PROCESS; OXYGEN; PERMEABILITY; PEROVSKITE; SEPARATION PROCESSES; STABILITY
OSTI ID:
21403577
Research Organizations:
Forschungszentrum Juelich GmbH (Germany). Inst. fuer Energieforschung (IEF), Werkstoffstruktur und Eigenschaften (IEF-2); Rheinisch-Westfaelische Technische Hochschule (RWTH), Aachen (Germany)
Country of Origin:
Germany
Language:
English
Other Identifying Numbers:
Other: ISBN 978-3-89336-581-4; ISSN 1866-1793; TRN: DE11G2371
Availability:
Commercial reproduction prohibited; OSTI as DE21403577
Submitting Site:
DE
Size:
197 pages
Announcement Date:
Mar 19, 2011

Citation Formats

Ellett, Anna Judith. Oxygen permeation and thermo-chemical stability of oxygen separation membrane materials for the oxyfuel process. Germany: N. p., 2009. Web.
Ellett, Anna Judith. Oxygen permeation and thermo-chemical stability of oxygen separation membrane materials for the oxyfuel process. Germany.
Ellett, Anna Judith. 2009. "Oxygen permeation and thermo-chemical stability of oxygen separation membrane materials for the oxyfuel process." Germany.
@misc{etde_21403577,
title = {Oxygen permeation and thermo-chemical stability of oxygen separation membrane materials for the oxyfuel process}
author = {Ellett, Anna Judith}
abstractNote = {The reduction of CO{sub 2} emissions, generally held to be one of the most significant contributors to global warming, is a major technological issue. CO{sub 2} Capture and Storage (CCS) techniques applied to large stationary sources such as coal-fired power plants could efficiently contribute to the global carbon mitigation effort. The oxyfuel process, which consists in the burning of coal in an oxygen-rich atmosphere to produce a flue gas highly concentrated in CO{sub 2}, is a technology considered for zero CO{sub 2} emission coal-fired power plants. The production of this O{sub 2}-rich combustion gas from air can be carried out using high purity oxygen separation membranes. Some of the most promising materials for this application are mixed ionic-electronic conducting (MIEC) materials with perovskite and K{sub 2}NiF{sub 4} perovskite-related structures. The present work examines the selection of La{sub 0.58}Sr{sub 0.4}Co{sub 0.2}Fe{sub 0.8}O{sub 3-{delta}} (LSCF58), La{sub 2}NiO{sub 4+{delta}}, Pr{sub 0.58}Sr{sub 0.4}Co{sub 0.2}Fe{sub 0.8}O{sub 3-{delta}} (PSCF58) and Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-{delta}} (BSCF50) as membrane materials for the separation of O{sub 2} and N{sub 2} in the framework of the oxyfuel process with flue gas recycling. Annealing experiments were carried out on pellets exposed to CO{sub 2}, water vapour, O{sub 2} and Cr{sub 2}O{sub 3} in order to determine the thermo-chemical resistance to the atmospheres and the high temperature conditions present during membrane operation in a coal-fired power plant. The degradation of their microstructure was investigated using Scanning Electron Microscopy (SEM) in combination with electron dispersive spectroscopy (EDS) as well as X-Ray Diffraction (XRD). Also, the oxygen permeation fluxes of selected membranes were investigated as a function of temperature. The membrane materials selected were characterised using thermo-analytical techniques such as precision thermogravimetric analysis (TGA) and thermo mechanical analysis (TMA). An increase in thermal expansion and oxygen permeation associated with an increase in oxygen vacancy concentration, observed also in the TGA curves, occurs during heating. BSCF50 exhibits permeation fluxes well above those of LSCF58, PSCF58 and La{sub 2}NiO{sub 4+{delta}}, which are quite similar to each other. After exposure, no degradation of LSCF58, La{sub 2}NiO{sub 4+{delta}} and PSCF58 occurs. On the other hand BSCF50 is found to be unstable in CO{sub 2}- and/or H{sub 2}O-containing atmospheres and also to exhibit a chemical demixing. The thermo-chemical stability and the oxygen permeation performances are both crucial factors in the selection of high purity oxygen separation membranes for the oxyfuel process, thus making LSCF58, PSCF58 and La{sub 2}NiO{sub 4+{delta}} in this study the most suitable materials for this application. Serious issues arise, however, from the fact that secondary non-ion conducting oxide phases are formed in the bulk of every material, forming obstacles for oxygen ion migration, and also that a reaction with chromia occurs, preventing their use without protection. (orig.)}
place = {Germany}
year = {2009}
month = {Jul}
}