Abstract
The surface crystallization and the dissolution rate of three phosphate glass compositions containing different amounts of niobium oxide were studied. The glasses were named Nb30, Nb37, and Nb44 according to the nominal content of niobium oxide in the glass composition. The three compositions were evaluated keeping the P{sub 2}O{sub 5}/K{sub 2}O ratio constant and varying the amount of Nb{sub 2}O{sub 5}. These glasses were produced by melting appropriate chemical compounds at 1500 deg C for 0.5 hour. The crystalline phases which were nucleated on the glass surface after heat treatment were determined by X-ray diffraction. The crystalline structures depend on the amount of niobium oxide in the glass composition. The crystal morphologies were observed by using an optical microscope, and their characteristics are specific for each kind of crystalline phase. The crystal growth rate and the surface nuclei density were determined for each glass composition, and they depend on each crystalline phase nucleated on the surface. From the differential thermal analysis curves it was determined that the Nb44 glass containing 46.5 mol por cent of niobium oxide is the most thermally stable against crystallization when compared to the Nb30 and Nb37 glasses. According to the activation energies determined for crystal
More>>
Citation Formats
Vieira, Heveline.
Study of the surface crystallization and resistance to dissolution of niobium phosphate glasses for nuclear waste immobilization; Estudo da cristalizacao superficial e da resistencia a dissolucao de vidros niobofosfatos visando a imobilizacao de rejeitos radioativos.
Brazil: N. p.,
2008.
Web.
Vieira, Heveline.
Study of the surface crystallization and resistance to dissolution of niobium phosphate glasses for nuclear waste immobilization; Estudo da cristalizacao superficial e da resistencia a dissolucao de vidros niobofosfatos visando a imobilizacao de rejeitos radioativos.
Brazil.
Vieira, Heveline.
2008.
"Study of the surface crystallization and resistance to dissolution of niobium phosphate glasses for nuclear waste immobilization; Estudo da cristalizacao superficial e da resistencia a dissolucao de vidros niobofosfatos visando a imobilizacao de rejeitos radioativos."
Brazil.
@misc{etde_21096965,
title = {Study of the surface crystallization and resistance to dissolution of niobium phosphate glasses for nuclear waste immobilization; Estudo da cristalizacao superficial e da resistencia a dissolucao de vidros niobofosfatos visando a imobilizacao de rejeitos radioativos}
author = {Vieira, Heveline}
abstractNote = {The surface crystallization and the dissolution rate of three phosphate glass compositions containing different amounts of niobium oxide were studied. The glasses were named Nb30, Nb37, and Nb44 according to the nominal content of niobium oxide in the glass composition. The three compositions were evaluated keeping the P{sub 2}O{sub 5}/K{sub 2}O ratio constant and varying the amount of Nb{sub 2}O{sub 5}. These glasses were produced by melting appropriate chemical compounds at 1500 deg C for 0.5 hour. The crystalline phases which were nucleated on the glass surface after heat treatment were determined by X-ray diffraction. The crystalline structures depend on the amount of niobium oxide in the glass composition. The crystal morphologies were observed by using an optical microscope, and their characteristics are specific for each kind of crystalline phase. The crystal growth rate and the surface nuclei density were determined for each glass composition, and they depend on each crystalline phase nucleated on the surface. From the differential thermal analysis curves it was determined that the Nb44 glass containing 46.5 mol por cent of niobium oxide is the most thermally stable against crystallization when compared to the Nb30 and Nb37 glasses. According to the activation energies determined for crystal growth on the surface of each glass type, the Nb44 glass can also be considered the most resistant one against crystallization. The dissolution rate for the Nb44 glass after 14 days immersed in an aqueous solution with pH equals to 7 at 90 deg C is the lowest (9.0 x 10{sup -7} g. cm{sup -2} . day{sup -1}) when compared to the other two glass compositions. The dissolution rates in acidic and neutral solutions of all studied glasses meet the international standards for materials which can be used in the immobilization of nuclear wastes. (author)}
place = {Brazil}
year = {2008}
month = {Jul}
}
title = {Study of the surface crystallization and resistance to dissolution of niobium phosphate glasses for nuclear waste immobilization; Estudo da cristalizacao superficial e da resistencia a dissolucao de vidros niobofosfatos visando a imobilizacao de rejeitos radioativos}
author = {Vieira, Heveline}
abstractNote = {The surface crystallization and the dissolution rate of three phosphate glass compositions containing different amounts of niobium oxide were studied. The glasses were named Nb30, Nb37, and Nb44 according to the nominal content of niobium oxide in the glass composition. The three compositions were evaluated keeping the P{sub 2}O{sub 5}/K{sub 2}O ratio constant and varying the amount of Nb{sub 2}O{sub 5}. These glasses were produced by melting appropriate chemical compounds at 1500 deg C for 0.5 hour. The crystalline phases which were nucleated on the glass surface after heat treatment were determined by X-ray diffraction. The crystalline structures depend on the amount of niobium oxide in the glass composition. The crystal morphologies were observed by using an optical microscope, and their characteristics are specific for each kind of crystalline phase. The crystal growth rate and the surface nuclei density were determined for each glass composition, and they depend on each crystalline phase nucleated on the surface. From the differential thermal analysis curves it was determined that the Nb44 glass containing 46.5 mol por cent of niobium oxide is the most thermally stable against crystallization when compared to the Nb30 and Nb37 glasses. According to the activation energies determined for crystal growth on the surface of each glass type, the Nb44 glass can also be considered the most resistant one against crystallization. The dissolution rate for the Nb44 glass after 14 days immersed in an aqueous solution with pH equals to 7 at 90 deg C is the lowest (9.0 x 10{sup -7} g. cm{sup -2} . day{sup -1}) when compared to the other two glass compositions. The dissolution rates in acidic and neutral solutions of all studied glasses meet the international standards for materials which can be used in the immobilization of nuclear wastes. (author)}
place = {Brazil}
year = {2008}
month = {Jul}
}