Abstract
The influence of different treatments on the aluminum system covered with aluminum oxide is investigated. The aluminum anodization in sulphuric media and in mixed sulphuric and phosphoric media was used to alter the corrosion resistance, thickness, coverage degree and microhardness of the anodic oxide. Iron electrodeposition inside the anodic oxide was used to change its electric conductivity and corrosion resistance. Direct and pulsed current were used for iron electrodeposition and the Fe(SO{sub 4}){sub 2}(NH{sub 4}){sub 2}.6H{sub 2}O electrolyte composition was changed with the addition of boric and ascorbic acids. To the sealing treatment the CeCl{sub 3} composition was varied. The energy dispersive x-ray (EDS), the x-ray fluorescence spectroscopy (FRX) and the morphologic analysis by scanning electronic microscopy (SEM) allowed to verify that, the pulsed current increase the iron content inside the anodic layer and that the use of the additives inhibits the iron oxidation. The chronopotentiometric curves obtained during iron electrodeposition indicated that the boric and ascorbic acids mixture increased the electrodeposition process efficiency. The electrochemical impedance spectroscopy (EIE), the Vickers (Hv) microhardness measurements and morphologic analysis evidenced that the sealing treatment improves the corrosion resistance of the anodic film modified with iron. The electrical impedance (EI) technique allowed to
More>>
Citation Formats
Souza, Kellie Provazi de.
The iron and cerium oxide influence on the electric conductivity and the corrosion resistance of anodized aluminium; A influencia do ferro e do oxido de cerio sobre a condutividade eletrica e a resistencia a corrosao do aluminio anodizado.
Brazil: N. p.,
2006.
Web.
Souza, Kellie Provazi de.
The iron and cerium oxide influence on the electric conductivity and the corrosion resistance of anodized aluminium; A influencia do ferro e do oxido de cerio sobre a condutividade eletrica e a resistencia a corrosao do aluminio anodizado.
Brazil.
Souza, Kellie Provazi de.
2006.
"The iron and cerium oxide influence on the electric conductivity and the corrosion resistance of anodized aluminium; A influencia do ferro e do oxido de cerio sobre a condutividade eletrica e a resistencia a corrosao do aluminio anodizado."
Brazil.
@misc{etde_20877913,
title = {The iron and cerium oxide influence on the electric conductivity and the corrosion resistance of anodized aluminium; A influencia do ferro e do oxido de cerio sobre a condutividade eletrica e a resistencia a corrosao do aluminio anodizado}
author = {Souza, Kellie Provazi de}
abstractNote = {The influence of different treatments on the aluminum system covered with aluminum oxide is investigated. The aluminum anodization in sulphuric media and in mixed sulphuric and phosphoric media was used to alter the corrosion resistance, thickness, coverage degree and microhardness of the anodic oxide. Iron electrodeposition inside the anodic oxide was used to change its electric conductivity and corrosion resistance. Direct and pulsed current were used for iron electrodeposition and the Fe(SO{sub 4}){sub 2}(NH{sub 4}){sub 2}.6H{sub 2}O electrolyte composition was changed with the addition of boric and ascorbic acids. To the sealing treatment the CeCl{sub 3} composition was varied. The energy dispersive x-ray (EDS), the x-ray fluorescence spectroscopy (FRX) and the morphologic analysis by scanning electronic microscopy (SEM) allowed to verify that, the pulsed current increase the iron content inside the anodic layer and that the use of the additives inhibits the iron oxidation. The chronopotentiometric curves obtained during iron electrodeposition indicated that the boric and ascorbic acids mixture increased the electrodeposition process efficiency. The electrochemical impedance spectroscopy (EIE), the Vickers (Hv) microhardness measurements and morphologic analysis evidenced that the sealing treatment improves the corrosion resistance of the anodic film modified with iron. The electrical impedance (EI) technique allowed to prove the electric conductivity increase of the anodized aluminum with iron electrodeposited even after the cerium low concentration treatment. Iron nanowires were prepared by using the anodic oxide pores as template. (author)}
place = {Brazil}
year = {2006}
month = {Jul}
}
title = {The iron and cerium oxide influence on the electric conductivity and the corrosion resistance of anodized aluminium; A influencia do ferro e do oxido de cerio sobre a condutividade eletrica e a resistencia a corrosao do aluminio anodizado}
author = {Souza, Kellie Provazi de}
abstractNote = {The influence of different treatments on the aluminum system covered with aluminum oxide is investigated. The aluminum anodization in sulphuric media and in mixed sulphuric and phosphoric media was used to alter the corrosion resistance, thickness, coverage degree and microhardness of the anodic oxide. Iron electrodeposition inside the anodic oxide was used to change its electric conductivity and corrosion resistance. Direct and pulsed current were used for iron electrodeposition and the Fe(SO{sub 4}){sub 2}(NH{sub 4}){sub 2}.6H{sub 2}O electrolyte composition was changed with the addition of boric and ascorbic acids. To the sealing treatment the CeCl{sub 3} composition was varied. The energy dispersive x-ray (EDS), the x-ray fluorescence spectroscopy (FRX) and the morphologic analysis by scanning electronic microscopy (SEM) allowed to verify that, the pulsed current increase the iron content inside the anodic layer and that the use of the additives inhibits the iron oxidation. The chronopotentiometric curves obtained during iron electrodeposition indicated that the boric and ascorbic acids mixture increased the electrodeposition process efficiency. The electrochemical impedance spectroscopy (EIE), the Vickers (Hv) microhardness measurements and morphologic analysis evidenced that the sealing treatment improves the corrosion resistance of the anodic film modified with iron. The electrical impedance (EI) technique allowed to prove the electric conductivity increase of the anodized aluminum with iron electrodeposited even after the cerium low concentration treatment. Iron nanowires were prepared by using the anodic oxide pores as template. (author)}
place = {Brazil}
year = {2006}
month = {Jul}
}