Study of the transformation of uranium-niobium alloys with low niobium concentrations, tempered from the gamma and beta + gamma 1 regions and then annealed at different temperatures. Comparison with uranium-molybdenum alloys (1963); Etude des transformations des alliages uranium-niobium a faible teneur en niobium trempes depuis les domaines gamma et beta + gamma 1 puis revenus a differentes temperatures. Comparaison avec les alliages uranium-molybdene (1963)

Abstract

The author shows that uranium-niobium alloys, like uranium-molybdenum alloys, tempered from the gamma region, give a martensitic phase with a structure deriving from that of alpha uranium by a slight contraction parallel to the axis [001], The critical cooling rate allowing the formation of this martensite is 80 deg. C/s at 750 deg. C. Retention of the beta phase of uranium-niobium alloys is particularly difficult, the critical retention rate being 700 deg. C/s at 668 deg. C for an alloy containing 2.5 at. per cent of Nb. This beta phase is completely converted to the alpha phase at room temperature in about 6 hours. The TTT curves of this beta alloy are effectively reduced to the lower branch of the lower 'C'. The beta phase conversion law is expressed as: 1-x = exp. (kt){sup n} x being the degree of progression of the conversion, t the time, n an exponent no-varying with temperature and having approximately the value 2 for the alloy considered, k an increasing function of temperature. The activation energy of conversion is of the order of 14,600 cal/mole. Niobium is much less active than molybdenum as a stabiliser of beta uranium. (author) [French] Dans ce travail l'auteur  More>>
Authors:
Collot, C [1] 
  1. Commissariat a l'Energie Atomique, Saclay (France). Centre d'Etudes Nucleaires
Publication Date:
Sep 15, 1962
Product Type:
Thesis/Dissertation
Report Number:
CEA-R-2341
Resource Relation:
Other Information: TH: These sciences; 25 refs
Subject:
36 MATERIALS SCIENCE; ACTIVATION ENERGY; BINARY ALLOY SYSTEMS; CRYSTAL-PHASE TRANSFORMATIONS; KINETICS; MICROSTRUCTURE; MOLYBDENUM ALLOYS; NIOBIUM ALLOYS; PHASE STUDIES; QUENCHING; URANIUM BASE ALLOYS
OSTI ID:
20818022
Research Organizations:
CEA Saclay, 91 - Gif-sur-Yvette (France); Faculte des Sciences de l'Universite de Nancy, 54 (France)
Country of Origin:
France
Language:
French
Other Identifying Numbers:
TRN: FR06R2341118151
Availability:
Available from INIS in electronic form
Submitting Site:
FRN
Size:
53 pages
Announcement Date:
Jan 04, 2007

Citation Formats

Collot, C. Study of the transformation of uranium-niobium alloys with low niobium concentrations, tempered from the gamma and beta + gamma 1 regions and then annealed at different temperatures. Comparison with uranium-molybdenum alloys (1963); Etude des transformations des alliages uranium-niobium a faible teneur en niobium trempes depuis les domaines gamma et beta + gamma 1 puis revenus a differentes temperatures. Comparaison avec les alliages uranium-molybdene (1963). France: N. p., 1962. Web.
Collot, C. Study of the transformation of uranium-niobium alloys with low niobium concentrations, tempered from the gamma and beta + gamma 1 regions and then annealed at different temperatures. Comparison with uranium-molybdenum alloys (1963); Etude des transformations des alliages uranium-niobium a faible teneur en niobium trempes depuis les domaines gamma et beta + gamma 1 puis revenus a differentes temperatures. Comparaison avec les alliages uranium-molybdene (1963). France.
Collot, C. 1962. "Study of the transformation of uranium-niobium alloys with low niobium concentrations, tempered from the gamma and beta + gamma 1 regions and then annealed at different temperatures. Comparison with uranium-molybdenum alloys (1963); Etude des transformations des alliages uranium-niobium a faible teneur en niobium trempes depuis les domaines gamma et beta + gamma 1 puis revenus a differentes temperatures. Comparaison avec les alliages uranium-molybdene (1963)." France.
@misc{etde_20818022,
title = {Study of the transformation of uranium-niobium alloys with low niobium concentrations, tempered from the gamma and beta + gamma 1 regions and then annealed at different temperatures. Comparison with uranium-molybdenum alloys (1963); Etude des transformations des alliages uranium-niobium a faible teneur en niobium trempes depuis les domaines gamma et beta + gamma 1 puis revenus a differentes temperatures. Comparaison avec les alliages uranium-molybdene (1963)}
author = {Collot, C}
abstractNote = {The author shows that uranium-niobium alloys, like uranium-molybdenum alloys, tempered from the gamma region, give a martensitic phase with a structure deriving from that of alpha uranium by a slight contraction parallel to the axis [001], The critical cooling rate allowing the formation of this martensite is 80 deg. C/s at 750 deg. C. Retention of the beta phase of uranium-niobium alloys is particularly difficult, the critical retention rate being 700 deg. C/s at 668 deg. C for an alloy containing 2.5 at. per cent of Nb. This beta phase is completely converted to the alpha phase at room temperature in about 6 hours. The TTT curves of this beta alloy are effectively reduced to the lower branch of the lower 'C'. The beta phase conversion law is expressed as: 1-x = exp. (kt){sup n} x being the degree of progression of the conversion, t the time, n an exponent no-varying with temperature and having approximately the value 2 for the alloy considered, k an increasing function of temperature. The activation energy of conversion is of the order of 14,600 cal/mole. Niobium is much less active than molybdenum as a stabiliser of beta uranium. (author) [French] Dans ce travail l'auteur montre que les alliages uranium-niobium, comme d'ailleurs les alliages uranium-molybdene, trempes depuis le domaine gamma, donnent une phase martensitique dont la structure derive de celle de l'uranium alpha par une legere contraction parallele de l'axe [001]. La vitesse critique de refroidissement permettant la formation de cette martensite est de 80 deg. C/s a 750 deg. C. La retention de la phase beta des alliages uranium-niobium est particulierement delicate car la vitesse critique de retention est de 700 deg. C/s a 668 deg. C pour l'alliage a 2,5 at. pour cent de Nb. Cette phase beta se transforme completement en phase alpha a la temperature ordinaire en 6 heures environ. Les courbes TTT de cet alliage de structure beta se reduisent pratiquement a la branche inferieure du 'C' inferieur. La loi de transformation de la phase beta s'ecrit: 1 exp. (kt){sup n} x est le degre d'avancement de la transformation, t le temps, n un exposant independant de la temperature et voisin de 2 pour l'alliage considere, k une fonction croissante de la temperature. L'energie d'activation de la transformation est de l'ordre de 14600 cal/mole. Le niobium est un stabilisant de l'uranium beta beaucoup moins actif que le molybdene. (auteur)}
place = {France}
year = {1962}
month = {Sep}
}