Abstract
Uranium dioxide powder used for studying the sintering process having grain size 63 {mu}. Sintering was performed in the temperature interval from 1000 - 1300 deg C in argon atmosphere. The O/U ratio of the used uranium dioxide was 2.07. Densities obtained by sintering under the mentioned conditions were not higher than 91% TG (theoretical density). This showed that the mentioned conditions were optimal, but the uranium dioxide obtained could be used for studying the radiation damage of fuel.
Ristic, M M
[1]
- Institute of Nuclear Sciences Vinca, Laboratorija za reaktorske materijale, Beograd (Serbia and Montenegro)
Citation Formats
Ristic, M M.
Study of the changes of uranium dioxide properties resulting from sintering; Izucavanje procesa sinterovanja urandioksida sa gledista promene karakteristicnih osobina.
Serbia and Montenegro: N. p.,
1962.
Web.
Ristic, M M.
Study of the changes of uranium dioxide properties resulting from sintering; Izucavanje procesa sinterovanja urandioksida sa gledista promene karakteristicnih osobina.
Serbia and Montenegro.
Ristic, M M.
1962.
"Study of the changes of uranium dioxide properties resulting from sintering; Izucavanje procesa sinterovanja urandioksida sa gledista promene karakteristicnih osobina."
Serbia and Montenegro.
@misc{etde_20808682,
title = {Study of the changes of uranium dioxide properties resulting from sintering; Izucavanje procesa sinterovanja urandioksida sa gledista promene karakteristicnih osobina}
author = {Ristic, M M}
abstractNote = {Uranium dioxide powder used for studying the sintering process having grain size 63 {mu}. Sintering was performed in the temperature interval from 1000 - 1300 deg C in argon atmosphere. The O/U ratio of the used uranium dioxide was 2.07. Densities obtained by sintering under the mentioned conditions were not higher than 91% TG (theoretical density). This showed that the mentioned conditions were optimal, but the uranium dioxide obtained could be used for studying the radiation damage of fuel.}
place = {Serbia and Montenegro}
year = {1962}
month = {Dec}
}
title = {Study of the changes of uranium dioxide properties resulting from sintering; Izucavanje procesa sinterovanja urandioksida sa gledista promene karakteristicnih osobina}
author = {Ristic, M M}
abstractNote = {Uranium dioxide powder used for studying the sintering process having grain size 63 {mu}. Sintering was performed in the temperature interval from 1000 - 1300 deg C in argon atmosphere. The O/U ratio of the used uranium dioxide was 2.07. Densities obtained by sintering under the mentioned conditions were not higher than 91% TG (theoretical density). This showed that the mentioned conditions were optimal, but the uranium dioxide obtained could be used for studying the radiation damage of fuel.}
place = {Serbia and Montenegro}
year = {1962}
month = {Dec}
}