We succeeded to prepare as-grown MgB{sub 2} superconducting thin films. The thin films were deposited on single crystal SrTiO{sub 3}(1 1 1) substrates by very simple method of rf-sputtering using a single target without post-annealing process. A Mg disk with many small chunks of B on it was used as a target. The temperature dependences of resistance were measured by the four-probe method and the films of substrate temperature during sputtering ranging from 100 to 120 deg. C showed zero resistivity at about 14 K.
Citation Formats
Ohkubo, H, and Akinaga, M.
Fabrication of as-grown superconducting MgB{sub 2} thin films.
Netherlands: N. p.,
2004.
Web.
doi:10.1016/j.physc.2004.03.153.
Ohkubo, H, & Akinaga, M.
Fabrication of as-grown superconducting MgB{sub 2} thin films.
Netherlands.
https://doi.org/10.1016/j.physc.2004.03.153
Ohkubo, H, and Akinaga, M.
2004.
"Fabrication of as-grown superconducting MgB{sub 2} thin films."
Netherlands.
https://doi.org/10.1016/j.physc.2004.03.153.
@misc{etde_20618409,
title = {Fabrication of as-grown superconducting MgB{sub 2} thin films}
author = {Ohkubo, H, and Akinaga, M}
abstractNote = {We succeeded to prepare as-grown MgB{sub 2} superconducting thin films. The thin films were deposited on single crystal SrTiO{sub 3}(1 1 1) substrates by very simple method of rf-sputtering using a single target without post-annealing process. A Mg disk with many small chunks of B on it was used as a target. The temperature dependences of resistance were measured by the four-probe method and the films of substrate temperature during sputtering ranging from 100 to 120 deg. C showed zero resistivity at about 14 K.}
doi = {10.1016/j.physc.2004.03.153}
journal = []
issue = {3-4}
volume = {408-410}
journal type = {AC}
place = {Netherlands}
year = {2004}
month = {Aug}
}
title = {Fabrication of as-grown superconducting MgB{sub 2} thin films}
author = {Ohkubo, H, and Akinaga, M}
abstractNote = {We succeeded to prepare as-grown MgB{sub 2} superconducting thin films. The thin films were deposited on single crystal SrTiO{sub 3}(1 1 1) substrates by very simple method of rf-sputtering using a single target without post-annealing process. A Mg disk with many small chunks of B on it was used as a target. The temperature dependences of resistance were measured by the four-probe method and the films of substrate temperature during sputtering ranging from 100 to 120 deg. C showed zero resistivity at about 14 K.}
doi = {10.1016/j.physc.2004.03.153}
journal = []
issue = {3-4}
volume = {408-410}
journal type = {AC}
place = {Netherlands}
year = {2004}
month = {Aug}
}