FY 1992 Report on results of the research and development of the technologies for forming composite materials. Development of the technologies for creating parts for high-efficiency power generation systems; 1992 nendo fukugo zairyo shinseikei gijutsu no kenkyu kaihatsu seika hokokusho. Kokoritsu hatsuden'yo buzai sosei gijutsu kaihatsu

Abstract

This project is aimed at development of the technologies for producing ceramic- and metal-based composite materials, and also technologies for superplastic processing by utilizing the phenomenon of superplasticity. The methods studied for development of the ceramic-based composites include casting and powder-utilizing forming at low temperature, and melt forming at high temperature. Those for the metal-based composites include melting at normal and high pressure, powder metallurgy type mechanical alloying and alkoxide methods. The composites studied for development of the superplastic processing are the whisker- and particle-reinforced ones. The composite reinforced with silicon nitride/SiC whiskers is found to be electrophoretically cast to have a bending strength of 497MPa at 1,250 degrees C. The parts of simple shape, e.g., rod and disk, having the target strength are produced by isostatically pressing at normal temperature and high pressure (CIP) and subsequently firing the granules, produced by spray drying the TiC particle/alumina-based slurry. (NEDO)
Authors:
"NONE"
Publication Date:
Mar 01, 1993
Product Type:
Technical Report
Report Number:
JP-NEDO-010015479
Resource Relation:
Other Information: PBD: Mar 1993
Subject:
36 MATERIALS SCIENCE; COMPOSITE MATERIALS; CERAMICS; METALS; WHISKERS; FIBERS; MOLDING; PLASTICITY; FRACTURE PROPERTIES; ALUMINIUM ALLOYS; ALUMINIUM OXIDES; POWDER METALLURGY; SINTERING; MATERIALS WORKING; HEAT RESISTANT MATERIALS
OSTI ID:
20175180
Research Organizations:
New Energy and Industrial Technology Development Organization, Tokyo (Japan)
Country of Origin:
Japan
Language:
Japanese
Other Identifying Numbers:
TRN: JN0140080
Availability:
Available to ETDE participating countries only(see www.etde.org); commercial reproduction prohibited; OSTI as DE20175180
Submitting Site:
NEDO
Size:
151 pages
Announcement Date:

Citation Formats

FY 1992 Report on results of the research and development of the technologies for forming composite materials. Development of the technologies for creating parts for high-efficiency power generation systems; 1992 nendo fukugo zairyo shinseikei gijutsu no kenkyu kaihatsu seika hokokusho. Kokoritsu hatsuden'yo buzai sosei gijutsu kaihatsu. Japan: N. p., 1993. Web.
FY 1992 Report on results of the research and development of the technologies for forming composite materials. Development of the technologies for creating parts for high-efficiency power generation systems; 1992 nendo fukugo zairyo shinseikei gijutsu no kenkyu kaihatsu seika hokokusho. Kokoritsu hatsuden'yo buzai sosei gijutsu kaihatsu. Japan.
1993. "FY 1992 Report on results of the research and development of the technologies for forming composite materials. Development of the technologies for creating parts for high-efficiency power generation systems; 1992 nendo fukugo zairyo shinseikei gijutsu no kenkyu kaihatsu seika hokokusho. Kokoritsu hatsuden'yo buzai sosei gijutsu kaihatsu." Japan.
@misc{etde_20175180,
title = {FY 1992 Report on results of the research and development of the technologies for forming composite materials. Development of the technologies for creating parts for high-efficiency power generation systems; 1992 nendo fukugo zairyo shinseikei gijutsu no kenkyu kaihatsu seika hokokusho. Kokoritsu hatsuden'yo buzai sosei gijutsu kaihatsu}
abstractNote = {This project is aimed at development of the technologies for producing ceramic- and metal-based composite materials, and also technologies for superplastic processing by utilizing the phenomenon of superplasticity. The methods studied for development of the ceramic-based composites include casting and powder-utilizing forming at low temperature, and melt forming at high temperature. Those for the metal-based composites include melting at normal and high pressure, powder metallurgy type mechanical alloying and alkoxide methods. The composites studied for development of the superplastic processing are the whisker- and particle-reinforced ones. The composite reinforced with silicon nitride/SiC whiskers is found to be electrophoretically cast to have a bending strength of 497MPa at 1,250 degrees C. The parts of simple shape, e.g., rod and disk, having the target strength are produced by isostatically pressing at normal temperature and high pressure (CIP) and subsequently firing the granules, produced by spray drying the TiC particle/alumina-based slurry. (NEDO)}
place = {Japan}
year = {1993}
month = {Mar}
}