Abstract
To carry out fatigue tests in sodium the experience gained in an ongoing program on irradiation effects was used for the definition of the test procedure and sample conditions, i.e. strain controlled experiments with an hour glass sample and axial strain measurement. In order to allow sodium corrosion to take place during the test, the samples were welded into a bellow and connected to a dynamic sodium loop. Due to the restricted test capacities, INTERATOM and the Metaalinstituut TNO (MI-TNO) pursued in a combined experimental program two different concepts with regard to the corrosion conditions. INTERATOM tested the samples during exposure in flowing sodium within a nonisothermal loop. The MI-TNO tested the samples after a precorrosion in a nonisothermal sodium loop. During the test at TNO the bellow-sealed samples were surrounded by static sodium.
Huthmann, H;
Menken, G;
[1]
Husslage, W
[2]
- INTERATOM, Bergisch Gladbach (Germany)
- TNO, Apeldoorn (Netherlands)
Citation Formats
Huthmann, H, Menken, G, and Husslage, W.
The fatigue behavior of X 6 CrNi 18 11 under sodium corrosion conditions.
IAEA: N. p.,
1977.
Web.
Huthmann, H, Menken, G, & Husslage, W.
The fatigue behavior of X 6 CrNi 18 11 under sodium corrosion conditions.
IAEA.
Huthmann, H, Menken, G, and Husslage, W.
1977.
"The fatigue behavior of X 6 CrNi 18 11 under sodium corrosion conditions."
IAEA.
@misc{etde_20156271,
title = {The fatigue behavior of X 6 CrNi 18 11 under sodium corrosion conditions}
author = {Huthmann, H, Menken, G, and Husslage, W}
abstractNote = {To carry out fatigue tests in sodium the experience gained in an ongoing program on irradiation effects was used for the definition of the test procedure and sample conditions, i.e. strain controlled experiments with an hour glass sample and axial strain measurement. In order to allow sodium corrosion to take place during the test, the samples were welded into a bellow and connected to a dynamic sodium loop. Due to the restricted test capacities, INTERATOM and the Metaalinstituut TNO (MI-TNO) pursued in a combined experimental program two different concepts with regard to the corrosion conditions. INTERATOM tested the samples during exposure in flowing sodium within a nonisothermal loop. The MI-TNO tested the samples after a precorrosion in a nonisothermal sodium loop. During the test at TNO the bellow-sealed samples were surrounded by static sodium.}
place = {IAEA}
year = {1977}
month = {Jul}
}
title = {The fatigue behavior of X 6 CrNi 18 11 under sodium corrosion conditions}
author = {Huthmann, H, Menken, G, and Husslage, W}
abstractNote = {To carry out fatigue tests in sodium the experience gained in an ongoing program on irradiation effects was used for the definition of the test procedure and sample conditions, i.e. strain controlled experiments with an hour glass sample and axial strain measurement. In order to allow sodium corrosion to take place during the test, the samples were welded into a bellow and connected to a dynamic sodium loop. Due to the restricted test capacities, INTERATOM and the Metaalinstituut TNO (MI-TNO) pursued in a combined experimental program two different concepts with regard to the corrosion conditions. INTERATOM tested the samples during exposure in flowing sodium within a nonisothermal loop. The MI-TNO tested the samples after a precorrosion in a nonisothermal sodium loop. During the test at TNO the bellow-sealed samples were surrounded by static sodium.}
place = {IAEA}
year = {1977}
month = {Jul}
}