The R and D project has been implemented for treating metal plating wastes (sludge) and aluminum dross in a melting furnace operated in a reducing atmosphere, in order to make the wastes harmless and recover the rare metals by the thermit reactions. The theoretical analysis of the powder properties has produced the desired powder pretreatment conditions, such as drying/firing conditions, mixing ratio and composition, forming conditions, and characteristics of the formed articles. For recovering the useful metals, it is confirmed that the thermit reactions proceed efficiently in a high-temperature melting furnace operated in a reducing atmosphere, and the molten metals are easily separated from the molten slag. It is also confirmed that the formed article allows separation of the metals from the residual slag more easily than the mixed powder. For the design of the continuous thermit reaction (CTR) system, it is investigated whether the products and other discharged substances can be safely handled and effectively utilized, and the control/instrumentation systems and others are established after setting the conditions for, e.g., sludge drying/firing in air, powder mixing/crushing, briquette production, and flow of the thermit reactions in a reducing atmosphere. (NEDO)
Citation Formats
None.
FY 1998 report on the result of R and D projects by local consortiums. Rare metal recovery and resourcing of residual slags from metal plating wastes and aluminum dross by continuous thermit reaction (CTR) system; 1998 nendo CTR (Continuous Termit Reaction) System ni yoru aluminium dross to mekki surajji kara no energy less, rare metal kaisei process to sono slag no saishigenka seika hokokusho.
Japan: N. p.,
2000.
Web.
None.
FY 1998 report on the result of R and D projects by local consortiums. Rare metal recovery and resourcing of residual slags from metal plating wastes and aluminum dross by continuous thermit reaction (CTR) system; 1998 nendo CTR (Continuous Termit Reaction) System ni yoru aluminium dross to mekki surajji kara no energy less, rare metal kaisei process to sono slag no saishigenka seika hokokusho.
Japan.
None.
2000.
"FY 1998 report on the result of R and D projects by local consortiums. Rare metal recovery and resourcing of residual slags from metal plating wastes and aluminum dross by continuous thermit reaction (CTR) system; 1998 nendo CTR (Continuous Termit Reaction) System ni yoru aluminium dross to mekki surajji kara no energy less, rare metal kaisei process to sono slag no saishigenka seika hokokusho."
Japan.
@misc{etde_20144964,
title = {FY 1998 report on the result of R and D projects by local consortiums. Rare metal recovery and resourcing of residual slags from metal plating wastes and aluminum dross by continuous thermit reaction (CTR) system; 1998 nendo CTR (Continuous Termit Reaction) System ni yoru aluminium dross to mekki surajji kara no energy less, rare metal kaisei process to sono slag no saishigenka seika hokokusho}
author = {None}
abstractNote = {The R and D project has been implemented for treating metal plating wastes (sludge) and aluminum dross in a melting furnace operated in a reducing atmosphere, in order to make the wastes harmless and recover the rare metals by the thermit reactions. The theoretical analysis of the powder properties has produced the desired powder pretreatment conditions, such as drying/firing conditions, mixing ratio and composition, forming conditions, and characteristics of the formed articles. For recovering the useful metals, it is confirmed that the thermit reactions proceed efficiently in a high-temperature melting furnace operated in a reducing atmosphere, and the molten metals are easily separated from the molten slag. It is also confirmed that the formed article allows separation of the metals from the residual slag more easily than the mixed powder. For the design of the continuous thermit reaction (CTR) system, it is investigated whether the products and other discharged substances can be safely handled and effectively utilized, and the control/instrumentation systems and others are established after setting the conditions for, e.g., sludge drying/firing in air, powder mixing/crushing, briquette production, and flow of the thermit reactions in a reducing atmosphere. (NEDO)}
place = {Japan}
year = {2000}
month = {Mar}
}
title = {FY 1998 report on the result of R and D projects by local consortiums. Rare metal recovery and resourcing of residual slags from metal plating wastes and aluminum dross by continuous thermit reaction (CTR) system; 1998 nendo CTR (Continuous Termit Reaction) System ni yoru aluminium dross to mekki surajji kara no energy less, rare metal kaisei process to sono slag no saishigenka seika hokokusho}
author = {None}
abstractNote = {The R and D project has been implemented for treating metal plating wastes (sludge) and aluminum dross in a melting furnace operated in a reducing atmosphere, in order to make the wastes harmless and recover the rare metals by the thermit reactions. The theoretical analysis of the powder properties has produced the desired powder pretreatment conditions, such as drying/firing conditions, mixing ratio and composition, forming conditions, and characteristics of the formed articles. For recovering the useful metals, it is confirmed that the thermit reactions proceed efficiently in a high-temperature melting furnace operated in a reducing atmosphere, and the molten metals are easily separated from the molten slag. It is also confirmed that the formed article allows separation of the metals from the residual slag more easily than the mixed powder. For the design of the continuous thermit reaction (CTR) system, it is investigated whether the products and other discharged substances can be safely handled and effectively utilized, and the control/instrumentation systems and others are established after setting the conditions for, e.g., sludge drying/firing in air, powder mixing/crushing, briquette production, and flow of the thermit reactions in a reducing atmosphere. (NEDO)}
place = {Japan}
year = {2000}
month = {Mar}
}