In September 1973 the sodium-cooled reactor KNK was shut down due to a steam generator tube damage. Failure location and results of the metallurgical examination of the damage are described. The cause of the damage is discussed. (author)
Citation Formats
Lorenz, H, and Herberg, G.
Post-failure metallurgical investigation of KNK steam generator tube damage.
IAEA: N. p.,
1975.
Web.
Lorenz, H, & Herberg, G.
Post-failure metallurgical investigation of KNK steam generator tube damage.
IAEA.
Lorenz, H, and Herberg, G.
1975.
"Post-failure metallurgical investigation of KNK steam generator tube damage."
IAEA.
@misc{etde_20107708,
title = {Post-failure metallurgical investigation of KNK steam generator tube damage}
author = {Lorenz, H, and Herberg, G}
abstractNote = {In September 1973 the sodium-cooled reactor KNK was shut down due to a steam generator tube damage. Failure location and results of the metallurgical examination of the damage are described. The cause of the damage is discussed. (author)}
place = {IAEA}
year = {1975}
month = {Jul}
}
title = {Post-failure metallurgical investigation of KNK steam generator tube damage}
author = {Lorenz, H, and Herberg, G}
abstractNote = {In September 1973 the sodium-cooled reactor KNK was shut down due to a steam generator tube damage. Failure location and results of the metallurgical examination of the damage are described. The cause of the damage is discussed. (author)}
place = {IAEA}
year = {1975}
month = {Jul}
}