Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on fuel cells (Research on aqueous alkaline solution electrolyte fuel cells); 1979 nendo nenryo denchi no kenkyu seika hokokusho. Arukari suiyoeki denkaishitsu nenryo denchi no kenkyu

Abstract

This paper describes achievements in fiscal 1979 in research on aqueous alkaline solution electrolyte fuel cells. Trial fabrication and tests for an oxygen electrode were performed on a catalytic electrode added with silver using carbonblack and graphites as carriers having excellent corrosion resistance and large surface area. Characteristics not inferior to electrodes using activated carbon as a carrier were obtained in both of the initial characteristics and continuous discharge characteristics. A platinum added electrode also showed the same performance as the silver added electrode. A hydrogen electrode containing Zr and iron among those containing Raney-Ni was found to have high oxidation resistance and stability in terms of life. A platinum added electrode using graphite as a carrier provided satisfactory initial characteristics as a hydrogen electrode. Research on a single cell construction has used and tested eight-cell laminated cells with an area of 1,000 cm{sup 2} using bipolar sheets made of carbon. The test verified appropriate the removal of produced water and heat using mainly the hydrogen circulation, which has been discussed in the summary design. The paper describes heat cycles, for which tests of ten and odds times in total were performed to have demonstrated that they are free of  More>>
Authors:
"NONE"
Publication Date:
Mar 01, 1980
Product Type:
Technical Report
Report Number:
JP-NEDO-010018330
Resource Relation:
Other Information: PBD: Mar 1980
Subject:
08 HYDROGEN; SUNSHINE PROJECT; ALKALINE ELECTROLYTE FUEL CELLS; ELECTRODES; CORROSION RESISTANCE; CARBON BLACK; GRAPHITE; STRATIFICATION; WATER REMOVAL; AFTER-HEAT REMOVAL; THERMAL CRACKING
OSTI ID:
20102524
Research Organizations:
New Energy and Industrial Technology Development Organization, Tokyo (Japan)
Country of Origin:
Japan
Language:
Japanese
Other Identifying Numbers:
TRN: JN0040285
Availability:
Available to ETDE participating countries only(see www.etde.org); commercial reproduction prohibited; OSTI as DE20102524
Submitting Site:
NEDO
Size:
216 pages
Announcement Date:

Citation Formats

Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on fuel cells (Research on aqueous alkaline solution electrolyte fuel cells); 1979 nendo nenryo denchi no kenkyu seika hokokusho. Arukari suiyoeki denkaishitsu nenryo denchi no kenkyu. Japan: N. p., 1980. Web.
Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on fuel cells (Research on aqueous alkaline solution electrolyte fuel cells); 1979 nendo nenryo denchi no kenkyu seika hokokusho. Arukari suiyoeki denkaishitsu nenryo denchi no kenkyu. Japan.
1980. "Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on fuel cells (Research on aqueous alkaline solution electrolyte fuel cells); 1979 nendo nenryo denchi no kenkyu seika hokokusho. Arukari suiyoeki denkaishitsu nenryo denchi no kenkyu." Japan.
@misc{etde_20102524,
title = {Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on fuel cells (Research on aqueous alkaline solution electrolyte fuel cells); 1979 nendo nenryo denchi no kenkyu seika hokokusho. Arukari suiyoeki denkaishitsu nenryo denchi no kenkyu}
abstractNote = {This paper describes achievements in fiscal 1979 in research on aqueous alkaline solution electrolyte fuel cells. Trial fabrication and tests for an oxygen electrode were performed on a catalytic electrode added with silver using carbonblack and graphites as carriers having excellent corrosion resistance and large surface area. Characteristics not inferior to electrodes using activated carbon as a carrier were obtained in both of the initial characteristics and continuous discharge characteristics. A platinum added electrode also showed the same performance as the silver added electrode. A hydrogen electrode containing Zr and iron among those containing Raney-Ni was found to have high oxidation resistance and stability in terms of life. A platinum added electrode using graphite as a carrier provided satisfactory initial characteristics as a hydrogen electrode. Research on a single cell construction has used and tested eight-cell laminated cells with an area of 1,000 cm{sup 2} using bipolar sheets made of carbon. The test verified appropriate the removal of produced water and heat using mainly the hydrogen circulation, which has been discussed in the summary design. The paper describes heat cycles, for which tests of ten and odds times in total were performed to have demonstrated that they are free of any anomaly. Furthermore, a manifold was attached as a means to improve the volume efficiency. Its function was also tested. (NEDO)}
place = {Japan}
year = {1980}
month = {Mar}
}