Abstract
From among researches on hydrogen manufacturing technologies using thermo-chemistry in the Sunshine Project, discussions were given on equipment materials, with the second-stage reaction in the iodine system cycle as the object. This paper describes achievements in fiscal 1979. The reaction produces MgO, I{sub 2} and O{sub 2} from Mg(IO{sub 3}){sub 2}. Corrosion tests were performed by using test pieces made of Ni alloy, iron-Ni-Cr alloy, Ti alloy, Zr alloy, Nb and Ta. These materials are thought to have excellent corrosion resistance in high temperature gaseous phase composed of iodine, oxygen and water. Corrosion tests were carried out also by using sheet formed test pieces of 24 kinds of alloys and six kinds of commercially available non-ferrous metallic materials in different temperatures and atmospheres, mainly the iodine plus oxygen plus H{sub 2}O mixed gas atmosphere at 600 degrees C. The corrosion resistance of the tested materials can be divided into three ranks. Materials having relatively good resistance were Ni-50Cr alloy and Co group alloy. Materials having good corrosion resistance are very little affected by water content. The higher the temperature, the more the metal corrosivity has increased. Preliminary discussions were given on pipe formability in materials having good corrosion resistance as
More>>
Citation Formats
None.
Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on hydrogen manufacturing technologies (Research on equipment materials for iodine system cycle); 1979 nendo netsukagakuho ni yoru suiso seizo gijutsu no kenkyu seika hokokusho. Yosokei cycle no sochi zairyo no kenkyu.
Japan: N. p.,
1980.
Web.
None.
Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on hydrogen manufacturing technologies (Research on equipment materials for iodine system cycle); 1979 nendo netsukagakuho ni yoru suiso seizo gijutsu no kenkyu seika hokokusho. Yosokei cycle no sochi zairyo no kenkyu.
Japan.
None.
1980.
"Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on hydrogen manufacturing technologies (Research on equipment materials for iodine system cycle); 1979 nendo netsukagakuho ni yoru suiso seizo gijutsu no kenkyu seika hokokusho. Yosokei cycle no sochi zairyo no kenkyu."
Japan.
@misc{etde_20102523,
title = {Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on hydrogen manufacturing technologies (Research on equipment materials for iodine system cycle); 1979 nendo netsukagakuho ni yoru suiso seizo gijutsu no kenkyu seika hokokusho. Yosokei cycle no sochi zairyo no kenkyu}
author = {None}
abstractNote = {From among researches on hydrogen manufacturing technologies using thermo-chemistry in the Sunshine Project, discussions were given on equipment materials, with the second-stage reaction in the iodine system cycle as the object. This paper describes achievements in fiscal 1979. The reaction produces MgO, I{sub 2} and O{sub 2} from Mg(IO{sub 3}){sub 2}. Corrosion tests were performed by using test pieces made of Ni alloy, iron-Ni-Cr alloy, Ti alloy, Zr alloy, Nb and Ta. These materials are thought to have excellent corrosion resistance in high temperature gaseous phase composed of iodine, oxygen and water. Corrosion tests were carried out also by using sheet formed test pieces of 24 kinds of alloys and six kinds of commercially available non-ferrous metallic materials in different temperatures and atmospheres, mainly the iodine plus oxygen plus H{sub 2}O mixed gas atmosphere at 600 degrees C. The corrosion resistance of the tested materials can be divided into three ranks. Materials having relatively good resistance were Ni-50Cr alloy and Co group alloy. Materials having good corrosion resistance are very little affected by water content. The higher the temperature, the more the metal corrosivity has increased. Preliminary discussions were given on pipe formability in materials having good corrosion resistance as the equipment piping materials. Their mechanical properties were also tested. This paper also describes corrosion resistance tests under heat transferring condition by using pipe-formed test pieces. (NEDO)}
place = {Japan}
year = {1980}
month = {Mar}
}
title = {Achievement report on research and development in the Sunshine Project in fiscal 1979. Research on hydrogen manufacturing technologies (Research on equipment materials for iodine system cycle); 1979 nendo netsukagakuho ni yoru suiso seizo gijutsu no kenkyu seika hokokusho. Yosokei cycle no sochi zairyo no kenkyu}
author = {None}
abstractNote = {From among researches on hydrogen manufacturing technologies using thermo-chemistry in the Sunshine Project, discussions were given on equipment materials, with the second-stage reaction in the iodine system cycle as the object. This paper describes achievements in fiscal 1979. The reaction produces MgO, I{sub 2} and O{sub 2} from Mg(IO{sub 3}){sub 2}. Corrosion tests were performed by using test pieces made of Ni alloy, iron-Ni-Cr alloy, Ti alloy, Zr alloy, Nb and Ta. These materials are thought to have excellent corrosion resistance in high temperature gaseous phase composed of iodine, oxygen and water. Corrosion tests were carried out also by using sheet formed test pieces of 24 kinds of alloys and six kinds of commercially available non-ferrous metallic materials in different temperatures and atmospheres, mainly the iodine plus oxygen plus H{sub 2}O mixed gas atmosphere at 600 degrees C. The corrosion resistance of the tested materials can be divided into three ranks. Materials having relatively good resistance were Ni-50Cr alloy and Co group alloy. Materials having good corrosion resistance are very little affected by water content. The higher the temperature, the more the metal corrosivity has increased. Preliminary discussions were given on pipe formability in materials having good corrosion resistance as the equipment piping materials. Their mechanical properties were also tested. This paper also describes corrosion resistance tests under heat transferring condition by using pipe-formed test pieces. (NEDO)}
place = {Japan}
year = {1980}
month = {Mar}
}