Abstract
As part of the research and development project for producing photovoltaic power generation systems at reduced cost, the R and D efforts are made for producing particle nonacceleration growth type silicon thin-film crystals. The research items are (1) research on thin-film crystals, and (2) research on cell-structuring method. The item (1) studies quantities, types and electrical properties of impurities and crystal defects in the polycrystalline ingots, produced by the Czochralski method from metal grade silicon and purified metal grade silicon stocks. Next, the substrate prepared above is coated with a thin film of silicon by the vapor-phase growth method with dichlorosilane as the source, to evaluate the thin-film crystals by measuring the crystal defects and lifetime of small numbers of carriers. The item (2) studies the effects of the solder dipping method. In addition, unevenness of photoelectric current is analyzed by a laser scanning microscope, to investigate the effects of the secondary impurities and crystal defects in the substrate crystals on photoelectric current. As a result, it is found that conversion efficiency is improved by grading the hole concentration in the p-type activated layer. The targets of 10 to 20 m{sup 2} as the area and 7 to 8% as
More>>
Citation Formats
None.
FY 1977 Annual report on Sunshine Project results. Research and development of photovoltaic power generation systems (Research and development of particle nonacceleration growth type silicon thin-film crystals); 1977 nendo taiyoko hatsuden system no kenkyu kaihatsu seika hokokusho. Ryushi hikasoku seichogata silicon usumaku kessho no kenkyu kaihatsu.
Japan: N. p.,
1978.
Web.
None.
FY 1977 Annual report on Sunshine Project results. Research and development of photovoltaic power generation systems (Research and development of particle nonacceleration growth type silicon thin-film crystals); 1977 nendo taiyoko hatsuden system no kenkyu kaihatsu seika hokokusho. Ryushi hikasoku seichogata silicon usumaku kessho no kenkyu kaihatsu.
Japan.
None.
1978.
"FY 1977 Annual report on Sunshine Project results. Research and development of photovoltaic power generation systems (Research and development of particle nonacceleration growth type silicon thin-film crystals); 1977 nendo taiyoko hatsuden system no kenkyu kaihatsu seika hokokusho. Ryushi hikasoku seichogata silicon usumaku kessho no kenkyu kaihatsu."
Japan.
@misc{etde_20094303,
title = {FY 1977 Annual report on Sunshine Project results. Research and development of photovoltaic power generation systems (Research and development of particle nonacceleration growth type silicon thin-film crystals); 1977 nendo taiyoko hatsuden system no kenkyu kaihatsu seika hokokusho. Ryushi hikasoku seichogata silicon usumaku kessho no kenkyu kaihatsu}
author = {None}
abstractNote = {As part of the research and development project for producing photovoltaic power generation systems at reduced cost, the R and D efforts are made for producing particle nonacceleration growth type silicon thin-film crystals. The research items are (1) research on thin-film crystals, and (2) research on cell-structuring method. The item (1) studies quantities, types and electrical properties of impurities and crystal defects in the polycrystalline ingots, produced by the Czochralski method from metal grade silicon and purified metal grade silicon stocks. Next, the substrate prepared above is coated with a thin film of silicon by the vapor-phase growth method with dichlorosilane as the source, to evaluate the thin-film crystals by measuring the crystal defects and lifetime of small numbers of carriers. The item (2) studies the effects of the solder dipping method. In addition, unevenness of photoelectric current is analyzed by a laser scanning microscope, to investigate the effects of the secondary impurities and crystal defects in the substrate crystals on photoelectric current. As a result, it is found that conversion efficiency is improved by grading the hole concentration in the p-type activated layer. The targets of 10 to 20 m{sup 2} as the area and 7 to 8% as the conversion efficiency are attained by preparing the crystals again. (NEDO)}
place = {Japan}
year = {1978}
month = {Mar}
}
title = {FY 1977 Annual report on Sunshine Project results. Research and development of photovoltaic power generation systems (Research and development of particle nonacceleration growth type silicon thin-film crystals); 1977 nendo taiyoko hatsuden system no kenkyu kaihatsu seika hokokusho. Ryushi hikasoku seichogata silicon usumaku kessho no kenkyu kaihatsu}
author = {None}
abstractNote = {As part of the research and development project for producing photovoltaic power generation systems at reduced cost, the R and D efforts are made for producing particle nonacceleration growth type silicon thin-film crystals. The research items are (1) research on thin-film crystals, and (2) research on cell-structuring method. The item (1) studies quantities, types and electrical properties of impurities and crystal defects in the polycrystalline ingots, produced by the Czochralski method from metal grade silicon and purified metal grade silicon stocks. Next, the substrate prepared above is coated with a thin film of silicon by the vapor-phase growth method with dichlorosilane as the source, to evaluate the thin-film crystals by measuring the crystal defects and lifetime of small numbers of carriers. The item (2) studies the effects of the solder dipping method. In addition, unevenness of photoelectric current is analyzed by a laser scanning microscope, to investigate the effects of the secondary impurities and crystal defects in the substrate crystals on photoelectric current. As a result, it is found that conversion efficiency is improved by grading the hole concentration in the p-type activated layer. The targets of 10 to 20 m{sup 2} as the area and 7 to 8% as the conversion efficiency are attained by preparing the crystals again. (NEDO)}
place = {Japan}
year = {1978}
month = {Mar}
}