This report describes the fiscal 1976 research result on solar heat collectors using glass system materials. In fiscal 1976, study was made on improvement of selective transmission films by vacuum deposition and large prototype films, prototype coated glass by chemical treatment and its quality stability, prototype full-scale honeycomb collector, practical heat collection property, and evaluation of some problems. As the study result, characteristics of this selective transmission glass were equivalent to those of the other selective transmission films with a transmissivity of 0.90 and a reflectivity of 0.10. As the study result of production cost by vacuum deposition and resistance heating, the film treatment cost was estimated to be 2,300yen/m{sup 2}. 40 prototype coated glass plates of 1,000 x 1,000 x 3mm, and 300 prototype coated glass pipes of 16mm diameter, 870mm long and 0.6mm thick were prepared for prototype collectors. Two kinds of full-scale collectors prepared by using these selective absorption heat collection plates and coated glass showed favorable performance in heat collection experiment. (NEDO)
Citation Formats
None.
Fiscal 1976 Sunshine Project result report. R and D on solar cooling/heating and hot water supply system (R and D on glass system materials); 1976 nendo taiyo reidanbo oyobi kyuto system no kenkyu kaihatsu seika hokokusho. Glass kei zairyo no kenkyu kaihatsu.
Japan: N. p.,
1977.
Web.
None.
Fiscal 1976 Sunshine Project result report. R and D on solar cooling/heating and hot water supply system (R and D on glass system materials); 1976 nendo taiyo reidanbo oyobi kyuto system no kenkyu kaihatsu seika hokokusho. Glass kei zairyo no kenkyu kaihatsu.
Japan.
None.
1977.
"Fiscal 1976 Sunshine Project result report. R and D on solar cooling/heating and hot water supply system (R and D on glass system materials); 1976 nendo taiyo reidanbo oyobi kyuto system no kenkyu kaihatsu seika hokokusho. Glass kei zairyo no kenkyu kaihatsu."
Japan.
@misc{etde_20093260,
title = {Fiscal 1976 Sunshine Project result report. R and D on solar cooling/heating and hot water supply system (R and D on glass system materials); 1976 nendo taiyo reidanbo oyobi kyuto system no kenkyu kaihatsu seika hokokusho. Glass kei zairyo no kenkyu kaihatsu}
author = {None}
abstractNote = {This report describes the fiscal 1976 research result on solar heat collectors using glass system materials. In fiscal 1976, study was made on improvement of selective transmission films by vacuum deposition and large prototype films, prototype coated glass by chemical treatment and its quality stability, prototype full-scale honeycomb collector, practical heat collection property, and evaluation of some problems. As the study result, characteristics of this selective transmission glass were equivalent to those of the other selective transmission films with a transmissivity of 0.90 and a reflectivity of 0.10. As the study result of production cost by vacuum deposition and resistance heating, the film treatment cost was estimated to be 2,300yen/m{sup 2}. 40 prototype coated glass plates of 1,000 x 1,000 x 3mm, and 300 prototype coated glass pipes of 16mm diameter, 870mm long and 0.6mm thick were prepared for prototype collectors. Two kinds of full-scale collectors prepared by using these selective absorption heat collection plates and coated glass showed favorable performance in heat collection experiment. (NEDO)}
place = {Japan}
year = {1977}
month = {Mar}
}
title = {Fiscal 1976 Sunshine Project result report. R and D on solar cooling/heating and hot water supply system (R and D on glass system materials); 1976 nendo taiyo reidanbo oyobi kyuto system no kenkyu kaihatsu seika hokokusho. Glass kei zairyo no kenkyu kaihatsu}
author = {None}
abstractNote = {This report describes the fiscal 1976 research result on solar heat collectors using glass system materials. In fiscal 1976, study was made on improvement of selective transmission films by vacuum deposition and large prototype films, prototype coated glass by chemical treatment and its quality stability, prototype full-scale honeycomb collector, practical heat collection property, and evaluation of some problems. As the study result, characteristics of this selective transmission glass were equivalent to those of the other selective transmission films with a transmissivity of 0.90 and a reflectivity of 0.10. As the study result of production cost by vacuum deposition and resistance heating, the film treatment cost was estimated to be 2,300yen/m{sup 2}. 40 prototype coated glass plates of 1,000 x 1,000 x 3mm, and 300 prototype coated glass pipes of 16mm diameter, 870mm long and 0.6mm thick were prepared for prototype collectors. Two kinds of full-scale collectors prepared by using these selective absorption heat collection plates and coated glass showed favorable performance in heat collection experiment. (NEDO)}
place = {Japan}
year = {1977}
month = {Mar}
}