This research and development is intended to establish a basic technology related to high crystalline polymeric material that has dynamic properties comparable to metallic materials by single polymeric material as a structural material. Thick and large high-elasticity molded forms were obtained by searching poly-arylate material, and by developing such processing technologies as high-pressure injection molding, composite injection molding, and elongation fluidity molding. High-elasticity molded forms with uniform internal orientation were obtained by heating and molding liquid crystal polymers under high magnetic field. Solution molding was performed on a molecular composite consisting of rigid chains and soft chains, which was laminated and bonded to have obtained an isotropic form with as high elasticity as 54 GPa. In addition, high pressure powder formation of cross-linked polymers of di-acetylene system provided an isotropic form with sound wave elasticity of 23 GPa.