Abstract
Phosphate glass containing 35 wt% simulated high level waste was prepared in 1966. This phosphate glass was crashed into 45 to 65 mesh in a agate mortar and crashed specimens were rinsed in carbon tetrachloride and ether three times each. The granular specimens held in the silver mesh baskets were leached in distilled water, tap water and sea water at room temperature from Mar. 1966 to Mar. 1983. Average leach rate of cesium and phosphorus in 17 years are {approx}10{sup -8} g/cm{sup 2} day. (author).
Kikuchi, Teruo;
[1]
Iwamoto, Kazumi
- Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment
Citation Formats
Kikuchi, Teruo, and Iwamoto, Kazumi.
Results of seventeen years leaching tests of simulated high level waste-phosphate glass.
Japan: N. p.,
1992.
Web.
Kikuchi, Teruo, & Iwamoto, Kazumi.
Results of seventeen years leaching tests of simulated high level waste-phosphate glass.
Japan.
Kikuchi, Teruo, and Iwamoto, Kazumi.
1992.
"Results of seventeen years leaching tests of simulated high level waste-phosphate glass."
Japan.
@misc{etde_10150861,
title = {Results of seventeen years leaching tests of simulated high level waste-phosphate glass}
author = {Kikuchi, Teruo, and Iwamoto, Kazumi}
abstractNote = {Phosphate glass containing 35 wt% simulated high level waste was prepared in 1966. This phosphate glass was crashed into 45 to 65 mesh in a agate mortar and crashed specimens were rinsed in carbon tetrachloride and ether three times each. The granular specimens held in the silver mesh baskets were leached in distilled water, tap water and sea water at room temperature from Mar. 1966 to Mar. 1983. Average leach rate of cesium and phosphorus in 17 years are {approx}10{sup -8} g/cm{sup 2} day. (author).}
place = {Japan}
year = {1992}
month = {Oct}
}
title = {Results of seventeen years leaching tests of simulated high level waste-phosphate glass}
author = {Kikuchi, Teruo, and Iwamoto, Kazumi}
abstractNote = {Phosphate glass containing 35 wt% simulated high level waste was prepared in 1966. This phosphate glass was crashed into 45 to 65 mesh in a agate mortar and crashed specimens were rinsed in carbon tetrachloride and ether three times each. The granular specimens held in the silver mesh baskets were leached in distilled water, tap water and sea water at room temperature from Mar. 1966 to Mar. 1983. Average leach rate of cesium and phosphorus in 17 years are {approx}10{sup -8} g/cm{sup 2} day. (author).}
place = {Japan}
year = {1992}
month = {Oct}
}