Pellets of the sintered ceramic, YBa/sub 2/Cu/sub 3/O/sub 7-y/, with three different oxygen contents, were irradiated with 6.5, 3.3 and 4.4 MeV fast neutron beams at fluences of 7.7*10/sup 5/, 1.3*10/sup 5/ and 1.4*10/sup 9/ n per square cm respectively. Radiation damage was investigated by comparing values of critical temperature (Tc-mid), zero resistivity and onset temperatures before and after neutron radiation. Critical current, as a function of temperature, was measured for some samples under the same experimental conditions. For all transport measurements, the different responses to the neutron radiation were observed and discussed.
Citation Formats
Mezzetti, E, Minetti, B, Abbattista, F, Vallino, M, Andreone, D, Lacquaniti, V, and Cherubini, R.
Low flux neutron irradiation of ceramic YBa/sub 2/Cu/sub 3/O/sub 7-y/.
Italy: N. p.,
1990.
Web.
Mezzetti, E, Minetti, B, Abbattista, F, Vallino, M, Andreone, D, Lacquaniti, V, & Cherubini, R.
Low flux neutron irradiation of ceramic YBa/sub 2/Cu/sub 3/O/sub 7-y/.
Italy.
Mezzetti, E, Minetti, B, Abbattista, F, Vallino, M, Andreone, D, Lacquaniti, V, and Cherubini, R.
1990.
"Low flux neutron irradiation of ceramic YBa/sub 2/Cu/sub 3/O/sub 7-y/."
Italy.
@misc{etde_10150001,
title = {Low flux neutron irradiation of ceramic YBa/sub 2/Cu/sub 3/O/sub 7-y/}
author = {Mezzetti, E, Minetti, B, Abbattista, F, Vallino, M, Andreone, D, Lacquaniti, V, and Cherubini, R}
abstractNote = {Pellets of the sintered ceramic, YBa/sub 2/Cu/sub 3/O/sub 7-y/, with three different oxygen contents, were irradiated with 6.5, 3.3 and 4.4 MeV fast neutron beams at fluences of 7.7*10/sup 5/, 1.3*10/sup 5/ and 1.4*10/sup 9/ n per square cm respectively. Radiation damage was investigated by comparing values of critical temperature (Tc-mid), zero resistivity and onset temperatures before and after neutron radiation. Critical current, as a function of temperature, was measured for some samples under the same experimental conditions. For all transport measurements, the different responses to the neutron radiation were observed and discussed.}
place = {Italy}
year = {1990}
month = {Dec}
}
title = {Low flux neutron irradiation of ceramic YBa/sub 2/Cu/sub 3/O/sub 7-y/}
author = {Mezzetti, E, Minetti, B, Abbattista, F, Vallino, M, Andreone, D, Lacquaniti, V, and Cherubini, R}
abstractNote = {Pellets of the sintered ceramic, YBa/sub 2/Cu/sub 3/O/sub 7-y/, with three different oxygen contents, were irradiated with 6.5, 3.3 and 4.4 MeV fast neutron beams at fluences of 7.7*10/sup 5/, 1.3*10/sup 5/ and 1.4*10/sup 9/ n per square cm respectively. Radiation damage was investigated by comparing values of critical temperature (Tc-mid), zero resistivity and onset temperatures before and after neutron radiation. Critical current, as a function of temperature, was measured for some samples under the same experimental conditions. For all transport measurements, the different responses to the neutron radiation were observed and discussed.}
place = {Italy}
year = {1990}
month = {Dec}
}