Abstract
Perovskite La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-powder with an Sr-content of 0.0 to 0.9 mole were produced by the solid-state reaction. They were plasma sprayed to fabricate coating samples and uniaxial pressing-sintering was used for shaping bodies. Sample properties investigated are stochiometry, crystal structure, phase transformation, thermal expansion, electrical conductivity up to 1000 C and the behavior of the powder during processing. Determined properties as a function of composition, oxygen and Mn{sup 4+}-ion concentration, temperature and processing method indicate that La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} materials with high electrical conductivity and a suitable coefficent of thermal expansion can be produced based on a definite crystal structure. These materials have a potential applicability in fabricating SOFC (Solid Oxide Fuel Cells). (orig.) [Deutsch] Perowskit La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-Pulver mit Sr-Gehalten von 0,0 bis 0,9 wurden durch Festkoerperreaktionen hergestellt. Sie wurden mittels Plasmaspritzen APS, NPS und VPS zu Schichten und ueber Pressen-Sintern zu Formkoerper verarbeitet. Die Eigenschaften der Proben: Stoechiometrie, Kristallstruktur, Phasenumwandlung, thermische Ausdehnung und elektrische Leitfaehigkeit bei Temperaturen bis 1000 C und das Verhalten der Pulver bei der Verarbeitung wurden ermittelt und charakterisiert. Aus den Untersuchungen der Eigenschaften in Abhaengigkeit von der chemischen Zusammensetzung, der Temperatur, dem Sauerstoff- und Mn{sup 4+}-Ionengehalt sowie den Verarbeitungsverfahren ergeben
More>>
Li, Z;
[1]
Stoever, D;
[1]
Scherberich, F D;
[2]
Behruzi, M;
[2]
Fuerst, L
[3]
- Forschungszentrum Juelich GmbH (Germany). Inst. fuer Angewandte Werkstofforschung
- Technische Hochschule Aachen (Germany). Lehrstuhl und Inst. fuer Kristallographie
- Forschungszentrum Juelich GmbH (Germany). Inst. fuer Chemie 4 - Angewandte Physikalische Chemie
Citation Formats
Li, Z, Stoever, D, Scherberich, F D, Behruzi, M, and Fuerst, L.
Perovskite La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} as cathode material for high-temperature fuel cells. Powder fabrication, shaping and characterization; Der Perowskit La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} als Kathodenwerkstoff fuer die Hochtemperatur-Brennstoffzelle; Pulverherstellung, Formgebung und Charakterisierung.
Germany: N. p.,
1993.
Web.
Li, Z, Stoever, D, Scherberich, F D, Behruzi, M, & Fuerst, L.
Perovskite La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} as cathode material for high-temperature fuel cells. Powder fabrication, shaping and characterization; Der Perowskit La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} als Kathodenwerkstoff fuer die Hochtemperatur-Brennstoffzelle; Pulverherstellung, Formgebung und Charakterisierung.
Germany.
Li, Z, Stoever, D, Scherberich, F D, Behruzi, M, and Fuerst, L.
1993.
"Perovskite La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} as cathode material for high-temperature fuel cells. Powder fabrication, shaping and characterization; Der Perowskit La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} als Kathodenwerkstoff fuer die Hochtemperatur-Brennstoffzelle; Pulverherstellung, Formgebung und Charakterisierung."
Germany.
@misc{etde_10137569,
title = {Perovskite La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} as cathode material for high-temperature fuel cells. Powder fabrication, shaping and characterization; Der Perowskit La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} als Kathodenwerkstoff fuer die Hochtemperatur-Brennstoffzelle; Pulverherstellung, Formgebung und Charakterisierung}
author = {Li, Z, Stoever, D, Scherberich, F D, Behruzi, M, and Fuerst, L}
abstractNote = {Perovskite La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-powder with an Sr-content of 0.0 to 0.9 mole were produced by the solid-state reaction. They were plasma sprayed to fabricate coating samples and uniaxial pressing-sintering was used for shaping bodies. Sample properties investigated are stochiometry, crystal structure, phase transformation, thermal expansion, electrical conductivity up to 1000 C and the behavior of the powder during processing. Determined properties as a function of composition, oxygen and Mn{sup 4+}-ion concentration, temperature and processing method indicate that La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} materials with high electrical conductivity and a suitable coefficent of thermal expansion can be produced based on a definite crystal structure. These materials have a potential applicability in fabricating SOFC (Solid Oxide Fuel Cells). (orig.) [Deutsch] Perowskit La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-Pulver mit Sr-Gehalten von 0,0 bis 0,9 wurden durch Festkoerperreaktionen hergestellt. Sie wurden mittels Plasmaspritzen APS, NPS und VPS zu Schichten und ueber Pressen-Sintern zu Formkoerper verarbeitet. Die Eigenschaften der Proben: Stoechiometrie, Kristallstruktur, Phasenumwandlung, thermische Ausdehnung und elektrische Leitfaehigkeit bei Temperaturen bis 1000 C und das Verhalten der Pulver bei der Verarbeitung wurden ermittelt und charakterisiert. Aus den Untersuchungen der Eigenschaften in Abhaengigkeit von der chemischen Zusammensetzung, der Temperatur, dem Sauerstoff- und Mn{sup 4+}-Ionengehalt sowie den Verarbeitungsverfahren ergeben sich Varianten der La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-Werkstoffe mit hoher elektrischer Leitfaehigkeit und passendem Thermausdehnungskoeffizienten, welche mit bestimmter Kristallstruktur verbunden sind. Diese La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-Varianten bieten ein Anwendungspotential fuer die Feststoffelektrolyt-Brennstoffzelle(SOFC). (orig.)}
place = {Germany}
year = {1993}
month = {Feb}
}
title = {Perovskite La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} as cathode material for high-temperature fuel cells. Powder fabrication, shaping and characterization; Der Perowskit La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} als Kathodenwerkstoff fuer die Hochtemperatur-Brennstoffzelle; Pulverherstellung, Formgebung und Charakterisierung}
author = {Li, Z, Stoever, D, Scherberich, F D, Behruzi, M, and Fuerst, L}
abstractNote = {Perovskite La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-powder with an Sr-content of 0.0 to 0.9 mole were produced by the solid-state reaction. They were plasma sprayed to fabricate coating samples and uniaxial pressing-sintering was used for shaping bodies. Sample properties investigated are stochiometry, crystal structure, phase transformation, thermal expansion, electrical conductivity up to 1000 C and the behavior of the powder during processing. Determined properties as a function of composition, oxygen and Mn{sup 4+}-ion concentration, temperature and processing method indicate that La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}} materials with high electrical conductivity and a suitable coefficent of thermal expansion can be produced based on a definite crystal structure. These materials have a potential applicability in fabricating SOFC (Solid Oxide Fuel Cells). (orig.) [Deutsch] Perowskit La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-Pulver mit Sr-Gehalten von 0,0 bis 0,9 wurden durch Festkoerperreaktionen hergestellt. Sie wurden mittels Plasmaspritzen APS, NPS und VPS zu Schichten und ueber Pressen-Sintern zu Formkoerper verarbeitet. Die Eigenschaften der Proben: Stoechiometrie, Kristallstruktur, Phasenumwandlung, thermische Ausdehnung und elektrische Leitfaehigkeit bei Temperaturen bis 1000 C und das Verhalten der Pulver bei der Verarbeitung wurden ermittelt und charakterisiert. Aus den Untersuchungen der Eigenschaften in Abhaengigkeit von der chemischen Zusammensetzung, der Temperatur, dem Sauerstoff- und Mn{sup 4+}-Ionengehalt sowie den Verarbeitungsverfahren ergeben sich Varianten der La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-Werkstoffe mit hoher elektrischer Leitfaehigkeit und passendem Thermausdehnungskoeffizienten, welche mit bestimmter Kristallstruktur verbunden sind. Diese La{sub 1-x}Sr{sub x}MnO{sub 3-{delta}}-Varianten bieten ein Anwendungspotential fuer die Feststoffelektrolyt-Brennstoffzelle(SOFC). (orig.)}
place = {Germany}
year = {1993}
month = {Feb}
}