Abstract
The relation existing between the stress corrosion behaviour and the fatigue-corrosion behaviour at low frequencies (inferior to 1 Hz), concerning initiation as well as propagation, of a 316L steel in a Mg Cl{sub 2} medium at 117 deg C, is studied. Fatigue-corrosion tests are realized using fixed amplitude traction-compression type stresses. The effects of stress frequency on rupture life and propagation speed, are studied. The damage kinetics study is completed with crack morphological observations realized with a specially developed optical technique. 2 figs., 2 refs.
Olive, J M;
Ranaivoarisoa, A;
Desjardins, D;
Puiggali, M
[1]
- Bordeaux-1 Univ., 33 - Talence (France)
Citation Formats
Olive, J M, Ranaivoarisoa, A, Desjardins, D, and Puiggali, M.
Characterization, at the mesoscopic and microscopic scales, of the low-frequency fatigue-corrosion damage in a 316L steel; Caracterisation aux echelles mesoscopiques et microscopique de l`endommagement par fatigue-corrosion basse frequence de l`acier 316L.
France: N. p.,
1994.
Web.
Olive, J M, Ranaivoarisoa, A, Desjardins, D, & Puiggali, M.
Characterization, at the mesoscopic and microscopic scales, of the low-frequency fatigue-corrosion damage in a 316L steel; Caracterisation aux echelles mesoscopiques et microscopique de l`endommagement par fatigue-corrosion basse frequence de l`acier 316L.
France.
Olive, J M, Ranaivoarisoa, A, Desjardins, D, and Puiggali, M.
1994.
"Characterization, at the mesoscopic and microscopic scales, of the low-frequency fatigue-corrosion damage in a 316L steel; Caracterisation aux echelles mesoscopiques et microscopique de l`endommagement par fatigue-corrosion basse frequence de l`acier 316L."
France.
@misc{etde_101361,
title = {Characterization, at the mesoscopic and microscopic scales, of the low-frequency fatigue-corrosion damage in a 316L steel; Caracterisation aux echelles mesoscopiques et microscopique de l`endommagement par fatigue-corrosion basse frequence de l`acier 316L}
author = {Olive, J M, Ranaivoarisoa, A, Desjardins, D, and Puiggali, M}
abstractNote = {The relation existing between the stress corrosion behaviour and the fatigue-corrosion behaviour at low frequencies (inferior to 1 Hz), concerning initiation as well as propagation, of a 316L steel in a Mg Cl{sub 2} medium at 117 deg C, is studied. Fatigue-corrosion tests are realized using fixed amplitude traction-compression type stresses. The effects of stress frequency on rupture life and propagation speed, are studied. The damage kinetics study is completed with crack morphological observations realized with a specially developed optical technique. 2 figs., 2 refs.}
journal = []
issue = {9}
volume = {91}
journal type = {AC}
place = {France}
year = {1994}
month = {Sep}
}
title = {Characterization, at the mesoscopic and microscopic scales, of the low-frequency fatigue-corrosion damage in a 316L steel; Caracterisation aux echelles mesoscopiques et microscopique de l`endommagement par fatigue-corrosion basse frequence de l`acier 316L}
author = {Olive, J M, Ranaivoarisoa, A, Desjardins, D, and Puiggali, M}
abstractNote = {The relation existing between the stress corrosion behaviour and the fatigue-corrosion behaviour at low frequencies (inferior to 1 Hz), concerning initiation as well as propagation, of a 316L steel in a Mg Cl{sub 2} medium at 117 deg C, is studied. Fatigue-corrosion tests are realized using fixed amplitude traction-compression type stresses. The effects of stress frequency on rupture life and propagation speed, are studied. The damage kinetics study is completed with crack morphological observations realized with a specially developed optical technique. 2 figs., 2 refs.}
journal = []
issue = {9}
volume = {91}
journal type = {AC}
place = {France}
year = {1994}
month = {Sep}
}