Abstract
Deuterium permeation measurements are suitable to characterize the integrity of layers, which are preoxidized or in-situ oxidized on high temperature alloys. The permeation through metal alloys with a growing oxidized layer is described by a model with a time dependence of the permeation flux related to the growth of the oxide layer. The behaviour of the layers, which are oxidized at different oxidizing atmospheres, are investigated in this work. By permeation test, parabolic rate constants, impeding factors, as well as permeability, diffusivity and the solubility of deuterium for the oxide layers are obtained. The measurement are continued in sulfidizing atmosphere for testing such layers as corrosion barrier. In correlation with microstructural post examinations it is found that permeation measurement can be utilized as a method for investigating high-temperature corrosion. (orig.) [Deutsch] Deuterium Permeationsmessungen sind geeignet die Integritaet der Schichten der voroxidierten oder in-situ oxidierten Hochtemperaturlegierung zu charakterisieren. Ueber Permeationsmessungen durch die Legierung kann das Wachstum von Oxidschichten bis zum stationaeren Zustand modelliert werden. Das Verhalten von Schichten, die unter verschiedenen oxidierenden Atmosphaeren gewachsen sind, ist in dieser Arbeit dargestellt. Beim Permeationstest wird die parabolische Wachstumkonstante, die Deuterium-Permeabilitaet, die Deuterium-Diffusionskonstante, die Deuterium-Loeslichkeit und der Hemmfaktor der Oxide bestimmt. Die Messungen werden
More>>
Citation Formats
Untoro, P.
Characterization of oxide layers of heat-resisting alloys in oxidizing and oxidizing/sulfidizing atmospheres by deuterium permeation measurement; Charakterisierung von Oxidschichten der Hochtemperaturlegierungen in oxidierenden und oxidierend/sulfidierenden Atmosphaeren durch Deuterium-Permeationsmessungen.
Germany: N. p.,
1993.
Web.
Untoro, P.
Characterization of oxide layers of heat-resisting alloys in oxidizing and oxidizing/sulfidizing atmospheres by deuterium permeation measurement; Charakterisierung von Oxidschichten der Hochtemperaturlegierungen in oxidierenden und oxidierend/sulfidierenden Atmosphaeren durch Deuterium-Permeationsmessungen.
Germany.
Untoro, P.
1993.
"Characterization of oxide layers of heat-resisting alloys in oxidizing and oxidizing/sulfidizing atmospheres by deuterium permeation measurement; Charakterisierung von Oxidschichten der Hochtemperaturlegierungen in oxidierenden und oxidierend/sulfidierenden Atmosphaeren durch Deuterium-Permeationsmessungen."
Germany.
@misc{etde_10129143,
title = {Characterization of oxide layers of heat-resisting alloys in oxidizing and oxidizing/sulfidizing atmospheres by deuterium permeation measurement; Charakterisierung von Oxidschichten der Hochtemperaturlegierungen in oxidierenden und oxidierend/sulfidierenden Atmosphaeren durch Deuterium-Permeationsmessungen}
author = {Untoro, P}
abstractNote = {Deuterium permeation measurements are suitable to characterize the integrity of layers, which are preoxidized or in-situ oxidized on high temperature alloys. The permeation through metal alloys with a growing oxidized layer is described by a model with a time dependence of the permeation flux related to the growth of the oxide layer. The behaviour of the layers, which are oxidized at different oxidizing atmospheres, are investigated in this work. By permeation test, parabolic rate constants, impeding factors, as well as permeability, diffusivity and the solubility of deuterium for the oxide layers are obtained. The measurement are continued in sulfidizing atmosphere for testing such layers as corrosion barrier. In correlation with microstructural post examinations it is found that permeation measurement can be utilized as a method for investigating high-temperature corrosion. (orig.) [Deutsch] Deuterium Permeationsmessungen sind geeignet die Integritaet der Schichten der voroxidierten oder in-situ oxidierten Hochtemperaturlegierung zu charakterisieren. Ueber Permeationsmessungen durch die Legierung kann das Wachstum von Oxidschichten bis zum stationaeren Zustand modelliert werden. Das Verhalten von Schichten, die unter verschiedenen oxidierenden Atmosphaeren gewachsen sind, ist in dieser Arbeit dargestellt. Beim Permeationstest wird die parabolische Wachstumkonstante, die Deuterium-Permeabilitaet, die Deuterium-Diffusionskonstante, die Deuterium-Loeslichkeit und der Hemmfaktor der Oxide bestimmt. Die Messungen werden weiter in sulfidierender Atmosphaere durchgefuehrt, um die Korrosionsbestaendigkeit der Schichten zu testen. Im Zusammenhang mit mikrostrukturellen Nachuntersuchungen konnten die Permeationsmessungen als Methode fuer die Untersuchung der Hochtemperatur-Korrosion nachgewiesen werden. (orig.)}
place = {Germany}
year = {1993}
month = {Feb}
}
title = {Characterization of oxide layers of heat-resisting alloys in oxidizing and oxidizing/sulfidizing atmospheres by deuterium permeation measurement; Charakterisierung von Oxidschichten der Hochtemperaturlegierungen in oxidierenden und oxidierend/sulfidierenden Atmosphaeren durch Deuterium-Permeationsmessungen}
author = {Untoro, P}
abstractNote = {Deuterium permeation measurements are suitable to characterize the integrity of layers, which are preoxidized or in-situ oxidized on high temperature alloys. The permeation through metal alloys with a growing oxidized layer is described by a model with a time dependence of the permeation flux related to the growth of the oxide layer. The behaviour of the layers, which are oxidized at different oxidizing atmospheres, are investigated in this work. By permeation test, parabolic rate constants, impeding factors, as well as permeability, diffusivity and the solubility of deuterium for the oxide layers are obtained. The measurement are continued in sulfidizing atmosphere for testing such layers as corrosion barrier. In correlation with microstructural post examinations it is found that permeation measurement can be utilized as a method for investigating high-temperature corrosion. (orig.) [Deutsch] Deuterium Permeationsmessungen sind geeignet die Integritaet der Schichten der voroxidierten oder in-situ oxidierten Hochtemperaturlegierung zu charakterisieren. Ueber Permeationsmessungen durch die Legierung kann das Wachstum von Oxidschichten bis zum stationaeren Zustand modelliert werden. Das Verhalten von Schichten, die unter verschiedenen oxidierenden Atmosphaeren gewachsen sind, ist in dieser Arbeit dargestellt. Beim Permeationstest wird die parabolische Wachstumkonstante, die Deuterium-Permeabilitaet, die Deuterium-Diffusionskonstante, die Deuterium-Loeslichkeit und der Hemmfaktor der Oxide bestimmt. Die Messungen werden weiter in sulfidierender Atmosphaere durchgefuehrt, um die Korrosionsbestaendigkeit der Schichten zu testen. Im Zusammenhang mit mikrostrukturellen Nachuntersuchungen konnten die Permeationsmessungen als Methode fuer die Untersuchung der Hochtemperatur-Korrosion nachgewiesen werden. (orig.)}
place = {Germany}
year = {1993}
month = {Feb}
}