The influence of hardening return, deformation ageing and {gamma}-irradiation on the Portevin-le-Chatelier effect in aluminium alloys: D16, D95, AK4, AK6 was investigated. It was shown, that the hardening temperature slightly influences on the discontinuous current nature, whereas the temperature and ageing on return causes the considerable changes of Portevin-le-Chatelier. It was shown that the irradiation of {gamma}-quantum low doses causes the Portevin-le-Chatelier effect in natural-aged state of alloy and disappearance of its effect during the subsequent ageing or during the irradiation with high doses. 6 refs.; 4 figs.; 2 tables. (author).
Citation Formats
Drobyazin, V N, Polovneva, S P, Podzirej, Yu S, Soldatenko, G A, and Vorob`ev, V G.
On problem about nature of Portevin-le-Chatelier effect in irradiated aluminium alloys; K voprosu o prirode ehffekta Portevena-le-Shatel`e v obluchennykh alyuminievykh splavakh.
Ukraine: N. p.,
1991.
Web.
Drobyazin, V N, Polovneva, S P, Podzirej, Yu S, Soldatenko, G A, & Vorob`ev, V G.
On problem about nature of Portevin-le-Chatelier effect in irradiated aluminium alloys; K voprosu o prirode ehffekta Portevena-le-Shatel`e v obluchennykh alyuminievykh splavakh.
Ukraine.
Drobyazin, V N, Polovneva, S P, Podzirej, Yu S, Soldatenko, G A, and Vorob`ev, V G.
1991.
"On problem about nature of Portevin-le-Chatelier effect in irradiated aluminium alloys; K voprosu o prirode ehffekta Portevena-le-Shatel`e v obluchennykh alyuminievykh splavakh."
Ukraine.
@misc{etde_10127688,
title = {On problem about nature of Portevin-le-Chatelier effect in irradiated aluminium alloys; K voprosu o prirode ehffekta Portevena-le-Shatel`e v obluchennykh alyuminievykh splavakh}
author = {Drobyazin, V N, Polovneva, S P, Podzirej, Yu S, Soldatenko, G A, and Vorob`ev, V G}
abstractNote = {The influence of hardening return, deformation ageing and {gamma}-irradiation on the Portevin-le-Chatelier effect in aluminium alloys: D16, D95, AK4, AK6 was investigated. It was shown, that the hardening temperature slightly influences on the discontinuous current nature, whereas the temperature and ageing on return causes the considerable changes of Portevin-le-Chatelier. It was shown that the irradiation of {gamma}-quantum low doses causes the Portevin-le-Chatelier effect in natural-aged state of alloy and disappearance of its effect during the subsequent ageing or during the irradiation with high doses. 6 refs.; 4 figs.; 2 tables. (author).}
place = {Ukraine}
year = {1991}
month = {Dec}
}
title = {On problem about nature of Portevin-le-Chatelier effect in irradiated aluminium alloys; K voprosu o prirode ehffekta Portevena-le-Shatel`e v obluchennykh alyuminievykh splavakh}
author = {Drobyazin, V N, Polovneva, S P, Podzirej, Yu S, Soldatenko, G A, and Vorob`ev, V G}
abstractNote = {The influence of hardening return, deformation ageing and {gamma}-irradiation on the Portevin-le-Chatelier effect in aluminium alloys: D16, D95, AK4, AK6 was investigated. It was shown, that the hardening temperature slightly influences on the discontinuous current nature, whereas the temperature and ageing on return causes the considerable changes of Portevin-le-Chatelier. It was shown that the irradiation of {gamma}-quantum low doses causes the Portevin-le-Chatelier effect in natural-aged state of alloy and disappearance of its effect during the subsequent ageing or during the irradiation with high doses. 6 refs.; 4 figs.; 2 tables. (author).}
place = {Ukraine}
year = {1991}
month = {Dec}
}