Abstract
This report presents the results of a number of investigations undertaken to characterise the MANET-II-Material (MArtensit for Next European Torus). It was delivered in the form of rods and plates, fabricated from 6 different heats. The transformation behaviour is described in the form of a time-temperature-transformation diagram (TTT) and the tempering behaviour by hardening (T = 850-1150 C) and tempering tests (T = 200-800 C). The dependence of the tensile strength upon tempering temperature (T = 200-800 C) and on the test-temperature (T = room temperature-750 C) was investigated. The creep and creep-rupture behaviour was determined for the temperature range between 450 and 700 C up to a maximum test-time of 10000 hours. The impact strength for different tempering conditions is presented in the form of A{sub v}-t-curves (T = -150-+200 C). (orig.) [Deutsch] Der Bericht beschreibt die Charakterisierungsarbeiten an dem MANET-II-Werkstoff (MArtensit for Next European Torus), der in 6 Einzelschmelzen und verschiedenen Halbzeugabmessungen (Staebe und Bleche) angeliefert wurde. Das Umwandlungsverhalten wird anhand des kontinuierlichen ZTU-Schaubildes und das Verguetungsverhalten durch Haerteversuche (T-Bereich 850-1150 C) und Anlassversuche (T = 200-800 C) beschrieben. Die Zugfestigkeitseigenschaften wurden in Abhaengigkeit von der Anlasstemperatur (200-800 C) und der Prueftemperatur (RT-750 C) ermittelt. Das Zeitstandfestigkeits- und
More>>
Citation Formats
Schirra, M, Graf, P, Heger, S, Meinzer, H, Schweiger, W, and Zimmermann, H.
MANET-II - investigation results on the transformation and tempering behaviour and examination on the mechanical properties; MANET-II, Untersuchungsergebnisse zum Umwandlungs- und Verguetungsverhalten und Pruefung mechanischer Eigenschaften.
Germany: N. p.,
1993.
Web.
Schirra, M, Graf, P, Heger, S, Meinzer, H, Schweiger, W, & Zimmermann, H.
MANET-II - investigation results on the transformation and tempering behaviour and examination on the mechanical properties; MANET-II, Untersuchungsergebnisse zum Umwandlungs- und Verguetungsverhalten und Pruefung mechanischer Eigenschaften.
Germany.
Schirra, M, Graf, P, Heger, S, Meinzer, H, Schweiger, W, and Zimmermann, H.
1993.
"MANET-II - investigation results on the transformation and tempering behaviour and examination on the mechanical properties; MANET-II, Untersuchungsergebnisse zum Umwandlungs- und Verguetungsverhalten und Pruefung mechanischer Eigenschaften."
Germany.
@misc{etde_10119828,
title = {MANET-II - investigation results on the transformation and tempering behaviour and examination on the mechanical properties; MANET-II, Untersuchungsergebnisse zum Umwandlungs- und Verguetungsverhalten und Pruefung mechanischer Eigenschaften}
author = {Schirra, M, Graf, P, Heger, S, Meinzer, H, Schweiger, W, and Zimmermann, H}
abstractNote = {This report presents the results of a number of investigations undertaken to characterise the MANET-II-Material (MArtensit for Next European Torus). It was delivered in the form of rods and plates, fabricated from 6 different heats. The transformation behaviour is described in the form of a time-temperature-transformation diagram (TTT) and the tempering behaviour by hardening (T = 850-1150 C) and tempering tests (T = 200-800 C). The dependence of the tensile strength upon tempering temperature (T = 200-800 C) and on the test-temperature (T = room temperature-750 C) was investigated. The creep and creep-rupture behaviour was determined for the temperature range between 450 and 700 C up to a maximum test-time of 10000 hours. The impact strength for different tempering conditions is presented in the form of A{sub v}-t-curves (T = -150-+200 C). (orig.) [Deutsch] Der Bericht beschreibt die Charakterisierungsarbeiten an dem MANET-II-Werkstoff (MArtensit for Next European Torus), der in 6 Einzelschmelzen und verschiedenen Halbzeugabmessungen (Staebe und Bleche) angeliefert wurde. Das Umwandlungsverhalten wird anhand des kontinuierlichen ZTU-Schaubildes und das Verguetungsverhalten durch Haerteversuche (T-Bereich 850-1150 C) und Anlassversuche (T = 200-800 C) beschrieben. Die Zugfestigkeitseigenschaften wurden in Abhaengigkeit von der Anlasstemperatur (200-800 C) und der Prueftemperatur (RT-750 C) ermittelt. Das Zeitstandfestigkeits- und Kriechverhalten wurde fuer den Temperaturbereich 450-700 C bis zu 10{sup 4} Std Standzeit bestimmt. Die Kerbschlagzaehigkeitseigenschaften wurden fuer mehrere Verguetungszustaende im T-Bereich -150 bis +200 C gemessen. (orig.)}
place = {Germany}
year = {1993}
month = {May}
}
title = {MANET-II - investigation results on the transformation and tempering behaviour and examination on the mechanical properties; MANET-II, Untersuchungsergebnisse zum Umwandlungs- und Verguetungsverhalten und Pruefung mechanischer Eigenschaften}
author = {Schirra, M, Graf, P, Heger, S, Meinzer, H, Schweiger, W, and Zimmermann, H}
abstractNote = {This report presents the results of a number of investigations undertaken to characterise the MANET-II-Material (MArtensit for Next European Torus). It was delivered in the form of rods and plates, fabricated from 6 different heats. The transformation behaviour is described in the form of a time-temperature-transformation diagram (TTT) and the tempering behaviour by hardening (T = 850-1150 C) and tempering tests (T = 200-800 C). The dependence of the tensile strength upon tempering temperature (T = 200-800 C) and on the test-temperature (T = room temperature-750 C) was investigated. The creep and creep-rupture behaviour was determined for the temperature range between 450 and 700 C up to a maximum test-time of 10000 hours. The impact strength for different tempering conditions is presented in the form of A{sub v}-t-curves (T = -150-+200 C). (orig.) [Deutsch] Der Bericht beschreibt die Charakterisierungsarbeiten an dem MANET-II-Werkstoff (MArtensit for Next European Torus), der in 6 Einzelschmelzen und verschiedenen Halbzeugabmessungen (Staebe und Bleche) angeliefert wurde. Das Umwandlungsverhalten wird anhand des kontinuierlichen ZTU-Schaubildes und das Verguetungsverhalten durch Haerteversuche (T-Bereich 850-1150 C) und Anlassversuche (T = 200-800 C) beschrieben. Die Zugfestigkeitseigenschaften wurden in Abhaengigkeit von der Anlasstemperatur (200-800 C) und der Prueftemperatur (RT-750 C) ermittelt. Das Zeitstandfestigkeits- und Kriechverhalten wurde fuer den Temperaturbereich 450-700 C bis zu 10{sup 4} Std Standzeit bestimmt. Die Kerbschlagzaehigkeitseigenschaften wurden fuer mehrere Verguetungszustaende im T-Bereich -150 bis +200 C gemessen. (orig.)}
place = {Germany}
year = {1993}
month = {May}
}