AC corrosion and cathodic protection - field experiments. Final report; Wechselstromkorrosion und kathodischer Schutz - Feldversuche. Abschlussbericht

Miscellaneous:

Abstract

The aim of the investigation is assessing the danger of corrosion of unalloyed steels by AC currents with the simultaneous effect of cathodic protection currents. This task was caused by cases of damage to cathodically protected pipelines, where an effect of AC due to stray currents from railway plant or by induction was present in the case of parallel high voltage lines. The effects of the medium, the density of AC and DC currents, the frequency and the operating conditions were examined in project F.5.4/24A (parts A1 and A2). The main points of the present part B were the construction and execution of a field experiment and measurements with potentio-static control of the potential with super-imposed simultaneous AC current. In addition, some orientated experiments were carried out on the effect of caotings and to determine the change of the IR-free potential of a sample caused by the AC current. (orig./MM). [Deutsch] Ziel der Untersuchung ist die Beurteilung der Korrosionsgefaehrdung von unlegierten Staehlen durch Wechselstroeme bei gleichzeitiger Einwirkung von kathodischen Schutzstroemen. Diese Aufgabenstellung wurde veranlasst durch Schadensfaelle an kathodisch geschuetzten Rohrleitungen, bei denen eine Wechselstrombeeinflussung durch Streustroeme von Bahnanlagen oder durch Induktion im Falle parallel fuehrender Hochspannungsleitungen vorlag. Die Einfluesse des  More>>
Publication Date:
Dec 31, 1992
Product Type:
Miscellaneous
Report Number:
ETDE-mf-93750629
Reference Number:
SCA: 032000; 360105; PA: DE-93:000132; SN: 93000915800
Resource Relation:
Other Information: PBD: 1992
Subject:
03 NATURAL GAS; 36 MATERIALS SCIENCE; CATHODIC PROTECTION; FAILURES; PIPELINES; CORROSION; ALTERNATING CURRENT; NATURAL GAS; STEELS; 032000; 360105; TRANSPORT, HANDLING, AND STORAGE; CORROSION AND EROSION
OSTI ID:
10112909
Research Organizations:
Ruhrgas AG, Essen (Germany)
Country of Origin:
Germany
Language:
German
Other Identifying Numbers:
Other: ON: DE93750629; CNN: Contract FE-KKs F 5.4/24 B; TRN: DE9300132
Availability:
OSTI; NTIS (US Sales Only)
Submitting Site:
DE
Size:
58 p.
Announcement Date:
Jun 30, 2005

Miscellaneous:

Citation Formats

None. AC corrosion and cathodic protection - field experiments. Final report; Wechselstromkorrosion und kathodischer Schutz - Feldversuche. Abschlussbericht. Germany: N. p., 1992. Web.
None. AC corrosion and cathodic protection - field experiments. Final report; Wechselstromkorrosion und kathodischer Schutz - Feldversuche. Abschlussbericht. Germany.
None. 1992. "AC corrosion and cathodic protection - field experiments. Final report; Wechselstromkorrosion und kathodischer Schutz - Feldversuche. Abschlussbericht." Germany.
@misc{etde_10112909,
title = {AC corrosion and cathodic protection - field experiments. Final report; Wechselstromkorrosion und kathodischer Schutz - Feldversuche. Abschlussbericht}
author = {None}
abstractNote = {The aim of the investigation is assessing the danger of corrosion of unalloyed steels by AC currents with the simultaneous effect of cathodic protection currents. This task was caused by cases of damage to cathodically protected pipelines, where an effect of AC due to stray currents from railway plant or by induction was present in the case of parallel high voltage lines. The effects of the medium, the density of AC and DC currents, the frequency and the operating conditions were examined in project F.5.4/24A (parts A1 and A2). The main points of the present part B were the construction and execution of a field experiment and measurements with potentio-static control of the potential with super-imposed simultaneous AC current. In addition, some orientated experiments were carried out on the effect of caotings and to determine the change of the IR-free potential of a sample caused by the AC current. (orig./MM). [Deutsch] Ziel der Untersuchung ist die Beurteilung der Korrosionsgefaehrdung von unlegierten Staehlen durch Wechselstroeme bei gleichzeitiger Einwirkung von kathodischen Schutzstroemen. Diese Aufgabenstellung wurde veranlasst durch Schadensfaelle an kathodisch geschuetzten Rohrleitungen, bei denen eine Wechselstrombeeinflussung durch Streustroeme von Bahnanlagen oder durch Induktion im Falle parallel fuehrender Hochspannungsleitungen vorlag. Die Einfluesse des Mediums, der Wechsel- und Gleichstromdichte, der Frequenz und der Betriebsbedingungen wurden in dem Projekt F.5.4/24A (Teile A1 und A2) untersucht. Schwerpunkte des vorliegenden B-Teiles waren Aufbau und Durchfuehrung eines Feldversuches sowie Messungen bei potentiostatischer Kontrolle des Potentials bei gleichzeitig ueberlagertem Wechselstrom. Zusaetzlich wurden einige orientierende Versuche zum Einfluss von Deckschichten und zur Bestimmung der durch den Wechselstrom hervorgerufenen Veraenderung des IR-freien Potentials einer Probe durchgefuehrt. (orig./MM).}
place = {Germany}
year = {1992}
month = {Dec}
}