Metallurgical and mechanical tests on the low activating martensitic chromium steel OPTIFER-IV; Metallkundliche und mechanische Untersuchungen an dem schwach aktivierbaren martensitischen Chromstahl OPTIFER-IV

Technical Report:

Abstract

Derived from a martensitic chromium-steel (1.4914) with high strength at elevated temperatures, a new low activating steel OPTIFER-IV, Chg. 986489, had been developed for an application as `First Wall` - and as structural material for fusion devices. The alloying elements with high activation like Mo, Ni and Nb had been substituted by similar acting, but low activating elements like W and Ta. Some metallurgical and mechanical properties had been tested in order to decide the kind of alloying. The new steel is fully martensitic without {delta}-ferrite, fine-grained and well hardenable. The tensile properties satisfy the requirements, and the notch impact bending properties are excellent. (orig.) [Deutsch] Ausgehend von dem hochwarmfesten martensitischen Chromstahl mit der Werkstoff-Nr. 1.4914 wurde durch Substitution der stark aktivierenden Legierungselemente Mo, Nb und Ni durch die wenig aktivierenden Elemente W, Ta und Ce und weitere metallurgische Veraenderungen ein nur schwach aktivierbarer martensitischer Stahl entwickelt, der sich in seiner zukuenftigen Form als Werkstoff fuer die Erste Wand und Blanketstrukturen von Fusionsmaschinen eignen soll. Der Stahl OPTIEFER-IV, Chg. 986489 wurde auf metallurgische und mechanische Eigenschaften untersucht. Das Umwandlungsverhalten der neuen Charge entspricht noch weitgehend dem des Vorgaengerstahles CETA. Der neue Stahl ist voll martensitisch, deltaferritfrei, feinkoernig und gut durchhaertbar.  More>>
Authors:
Schaefer, L; [1]  Kempe, H [1] 
  1. Kernforschungszentrum Karlsruhe GmbH (Germany). Projekt Kernfusion
Publication Date:
Aug 01, 1994
Product Type:
Technical Report
Report Number:
KFK-5353
Reference Number:
SCA: 360103; 700480; PA: DEN-95:0F0565; EDB-95:022483; SN: 95001321377
Resource Relation:
Other Information: PBD: Aug 1994
Subject:
36 MATERIALS SCIENCE; 70 PLASMA PHYSICS AND FUSION TECHNOLOGY; MARTENSITIC STEELS; OPTIMIZATION; MECHANICAL PROPERTIES; THERMONUCLEAR REACTOR MATERIALS; TUNGSTEN ALLOYS; TANTALUM ADDITIONS; 360103; 700480; COMPONENT DEVELOPMENT; MATERIALS STUDIES
OSTI ID:
10110222
Research Organizations:
Kernforschungszentrum Karlsruhe GmbH (Germany). Projekt Kernfusion; Kernforschungszentrum Karlsruhe GmbH (Germany). Inst. fuer Materialforschung
Country of Origin:
Germany
Language:
German
Other Identifying Numbers:
Journal ID: ISSN 0303-4003; Other: ON: DE95738282; TRN: DE95F0565
Availability:
OSTI; NTIS (US Sales Only); INIS
Submitting Site:
DEN
Size:
28 p.
Announcement Date:
Jun 30, 2005

Technical Report:

Citation Formats

Schaefer, L, and Kempe, H. Metallurgical and mechanical tests on the low activating martensitic chromium steel OPTIFER-IV; Metallkundliche und mechanische Untersuchungen an dem schwach aktivierbaren martensitischen Chromstahl OPTIFER-IV. Germany: N. p., 1994. Web.
Schaefer, L, & Kempe, H. Metallurgical and mechanical tests on the low activating martensitic chromium steel OPTIFER-IV; Metallkundliche und mechanische Untersuchungen an dem schwach aktivierbaren martensitischen Chromstahl OPTIFER-IV. Germany.
Schaefer, L, and Kempe, H. 1994. "Metallurgical and mechanical tests on the low activating martensitic chromium steel OPTIFER-IV; Metallkundliche und mechanische Untersuchungen an dem schwach aktivierbaren martensitischen Chromstahl OPTIFER-IV." Germany.
@misc{etde_10110222,
title = {Metallurgical and mechanical tests on the low activating martensitic chromium steel OPTIFER-IV; Metallkundliche und mechanische Untersuchungen an dem schwach aktivierbaren martensitischen Chromstahl OPTIFER-IV}
author = {Schaefer, L, and Kempe, H}
abstractNote = {Derived from a martensitic chromium-steel (1.4914) with high strength at elevated temperatures, a new low activating steel OPTIFER-IV, Chg. 986489, had been developed for an application as `First Wall` - and as structural material for fusion devices. The alloying elements with high activation like Mo, Ni and Nb had been substituted by similar acting, but low activating elements like W and Ta. Some metallurgical and mechanical properties had been tested in order to decide the kind of alloying. The new steel is fully martensitic without {delta}-ferrite, fine-grained and well hardenable. The tensile properties satisfy the requirements, and the notch impact bending properties are excellent. (orig.) [Deutsch] Ausgehend von dem hochwarmfesten martensitischen Chromstahl mit der Werkstoff-Nr. 1.4914 wurde durch Substitution der stark aktivierenden Legierungselemente Mo, Nb und Ni durch die wenig aktivierenden Elemente W, Ta und Ce und weitere metallurgische Veraenderungen ein nur schwach aktivierbarer martensitischer Stahl entwickelt, der sich in seiner zukuenftigen Form als Werkstoff fuer die Erste Wand und Blanketstrukturen von Fusionsmaschinen eignen soll. Der Stahl OPTIEFER-IV, Chg. 986489 wurde auf metallurgische und mechanische Eigenschaften untersucht. Das Umwandlungsverhalten der neuen Charge entspricht noch weitgehend dem des Vorgaengerstahles CETA. Der neue Stahl ist voll martensitisch, deltaferritfrei, feinkoernig und gut durchhaertbar. Die Zugeigenschaften entsprechen den Anforderungen, un die Kerbschlageigenschaften sind hervorragend. (orig.)}
place = {Germany}
year = {1994}
month = {Aug}
}