Phase diagram of the Fe-Co-Ti system at 1073 K Kozakai, T; Koyama, T; Doi, M; Miyazaki, T [Nagoya Inst. of Tech. (Japan). Dept. of Materials Science and Engineering]; Kobayashi, M [Graduate School, Nagoya Inst. of Tech. (Japan)] 36 MATERIALS SCIENCE; PHASE DIAGRAMS; IRON ALLOYS; COBALT ALLOYS; TITANIUM ALLOYS; TEMPERATURE RANGE 1000-4000 K; X-RAY DIFFRACTION; TRANSMISSION ELECTRON MICROSCOPY; SOLID SOLUTIONS; INTERMETALLIC COMPOUNDS; LAVES PHASES The phase equilibria in the Fe-Co-Ti system were investigated at 1073 K by means of X-ray diffraction, transmission electron microscopy, and in situ energy-dispersive spectroscopy. Four three-phase and eleven two-phase microstructures, consisting of disordered solid solutions, B2 ordered intermetallics, Laves phases, and L1{sub 2} ordered phase, were observed. On the basis of the experimental results and the chemical analyses of the coexisting phases, an isothermal section at 1073 K is proposed, which is similar to the section at 1173 K reported in the literature. (orig.) Germany 2002-03-01 English Journal Article Journal Name: Zeitschrift fuer Metallkunde; Journal Volume: 93; Journal Issue: 3; Other Information: PBD: Mar 2002 Medium: X; Size: page(s) 199-203 https://doi.org/ [] 3 93 Journal ID: ISSN 0044-3093; ZEMTAE; TRN: DE02G3974 DE 2010-12-30 20241186