Method for preparing ceramic composite
Abstract
A process for preparing ceramic composite comprising blending TiC particulates, Al.sub.2 O.sub.3 particulates and nickle aluminide and consolidating the mixture at a temperature and pressure sufficient to produce a densified ceramic composite having fracture toughness equal to or greater than 7 MPa m.sup.1/2, a hardness equal to or greater than 18 GPa.
- Inventors:
-
- Oak Ridge, TN
- Lenoir City, TN
- Knoxville, TN
- Issue Date:
- Research Org.:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- OSTI Identifier:
- 870240
- Patent Number(s):
- 5482673
- Assignee:
- Martin Marietta Energy Systems, Inc. (Oak Ridge, TN)
- Patent Classifications (CPCs):
-
C - CHEMISTRY C22 - METALLURGY C22C - ALLOYS
- DOE Contract Number:
- AC05-84OR21400
- Resource Type:
- Patent
- Country of Publication:
- United States
- Language:
- English
- Subject:
- method; preparing; ceramic; composite; process; comprising; blending; tic; particulates; nickle; aluminide; consolidating; mixture; temperature; pressure; sufficient; produce; densified; fracture; toughness; equal; mpa; hardness; 18; gpa; ceramic composite; fracture toughness; composite comprising; pressure sufficient; preparing ceramic; densified ceramic; /419/75/
Citation Formats
Alexander, Kathleen B, Tiegs, Terry N, Becher, Paul F, and Waters, Shirley B. Method for preparing ceramic composite. United States: N. p., 1996.
Web.
Alexander, Kathleen B, Tiegs, Terry N, Becher, Paul F, & Waters, Shirley B. Method for preparing ceramic composite. United States.
Alexander, Kathleen B, Tiegs, Terry N, Becher, Paul F, and Waters, Shirley B. Mon .
"Method for preparing ceramic composite". United States. https://www.osti.gov/servlets/purl/870240.
@article{osti_870240,
title = {Method for preparing ceramic composite},
author = {Alexander, Kathleen B and Tiegs, Terry N and Becher, Paul F and Waters, Shirley B},
abstractNote = {A process for preparing ceramic composite comprising blending TiC particulates, Al.sub.2 O.sub.3 particulates and nickle aluminide and consolidating the mixture at a temperature and pressure sufficient to produce a densified ceramic composite having fracture toughness equal to or greater than 7 MPa m.sup.1/2, a hardness equal to or greater than 18 GPa.},
doi = {},
journal = {},
number = ,
volume = ,
place = {United States},
year = {Mon Jan 01 00:00:00 EST 1996},
month = {Mon Jan 01 00:00:00 EST 1996}
}
Save to My Library
You must Sign In or Create an Account in order to save documents to your library.
Works referenced in this record:
Rapid Rate Sintering of AI 2 O 3 -TiC Composites for Cutting-Tool Applications
journal, January 1988
- Lee, Minyoung; Borom, Marcus P.
- Advanced Ceramic Materials, Vol. 3, Issue 1
Alumina ceramics with particle inclusions
journal, January 1993
- Ekström, Thommy
- Journal of the European Ceramic Society, Vol. 11, Issue 6
Sol-gel prepared Ni-alumina composite materials: Part I Microstructure and mechanical properties
journal, March 1992
- Breval, E.; Deng, Z.; Chiou, S.
- Journal of Materials Science, Vol. 27, Issue 6
Fracture behaviour of composites based on Al2O3-TiC
journal, April 1980
- Wahi, R. P.; Ilschner, B.
- Journal of Materials Science, Vol. 15, Issue 4
Pressureless-sintered Al2O3-TiC composites
journal, November 1988
- Cutler, Raymond A.; Hurford, Andrew C.; Virkar, Anil V.
- Materials Science and Engineering: A, Vol. 105-106
The toughening of alumina with nickel inclusions
journal, January 1990
- Tuan, W. H.; Brook, R. J.
- Journal of the European Ceramic Society, Vol. 6, Issue 1
Processing of alumina/nickel composites
journal, January 1992
- Tuan, W. H.; Brook, R. J.
- Journal of the European Ceramic Society, Vol. 10, Issue 2