Post-test evaluation of oxygen electrodes from solid oxide electrolysis stacks.
The oxygen electrodes from two solid oxide electrolysis stacks that performed high-temperature steam electrolysis (HTSE) and produced hydrogen for 1000 and 2000 h, respectively, were examined using X-ray fluorescence, X-ray absorption near edge structure (XANES), four-point resistivity, scanning electron microscopy, energy dispersive spectroscopy, X-ray diffraction and Raman micro-spectroscopy to determine possible causes for the degradation in stack performance over the test periods. These techniques yielded information such as elemental distribution, oxidation state, phases present, electrode delamination, and porosity within the electrode layers. From these studies, we found two phenomena that were likely the cause of increasingly poor oxygen electrode performance over time. The first source of degradation was chromium substitution into the oxygen electrode bond layer, which serves to bond the cell to the flow field and interconnect. This is caused by migration of a chromium species from the bipolar plate. The effect of this is a significant increase in the electrical resistance of the bond layer material. The other source of degradation identified was oxygen electrode delamination. The cause of electrode delamination, which is locally catastrophic to the operation of the cell, is unclear; however, we will discuss two possible mechanisms that might cause this phenomenon.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- NE; USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 973022
- Report Number(s):
- ANL/CSE/JA-61131; IJHEDX; TRN: US201005%%511
- Journal Information:
- Int. J. Hydrogen Energy, Vol. 34, Issue 9 ; May 2009; ISSN 0360-3199
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
DEGRADATION ISSUES IN SOLID OXIDE CELLS DURING HIGH TEMPERATURE ELECTROLYSIS
DEGRADATION ISSUES IN SOLID OXIDE CELLS DURING HIGH TEMPERATURE ELECTROLYSIS