Development of Alumina-Forming Austenitic Stainless Steels
- ORNL
Work in fiscal year 2008 focused on the development of creep-resistant, alumina-forming austenitic (AFA) stainless steel alloys, which exhibit a unique combination of an excellent oxidation resistance via protective alumina (Al2O3) scale formation and high-temperature creep strength through the formation of stable nano-scale MC carbides [1-8]. High levels of Nb additions (> 1 wt.% Nb) and/or Ni additions (25-30 wt.%), at Al levels of 2.5-4 wt.%, were found to correlate with increased upper-temperature limit for Al2O3 scale formation in air ( 900 aC) and air with 10% water vapor ( 800 aC). Creep resistance also showed a strong dependence on the level of Nb additions, and was correlated with volume fraction of MC-type carbides using thermodynamic computational tools. A trial heat of a 50 lb AFA alloy ingot was made using conventional single-melt vacuum techniques, and the alloy was successfully hot-rolled without any cracking [2]. This heat showed good weldability, using filler material of the same alloy.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Shared Research Equipment Collaborative Research Center
- Sponsoring Organization:
- FE USDOE - Office of Fossil Energy (FE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 969007
- Resource Relation:
- Conference: 22nd Annual Conference on Fossil Energy Materials, Pittsburgh, PA, USA, 20080708, 20080708
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of Alumina-Forming Austenitic Stainless Steels
Development and Exploratory Scale-Up of Alumina-Forming Austenitic (AFA) Stainless Steels