Oxidation behavior of copper at high temperatures under two different modes of direct-current applications
- Indian Institute of Technology, Kharagpur (India)
Oxidation kinetics of copper in the temperature range of 973-1173 K at P{sub o{sub 2}}=21.27 kPa exhibit enhancement and deceleration in the rates with changing polarity compared to normal oxidation under interrupted mode of direct-current application. These conditions are achieved by connecting the oxidizing copper covered with an initially formed thin oxide film to the positive and negative terminal of a dc source, respectively. However, the influence of direction of the current is found to be opposite under uninterrupted mode of impressed current flow in the same temperature range. The effect of short-circuiting the metal to the outer oxide/air interface on the reaction kinetics is also reported. The rate of oxide-scale growth under normal condition, and two different modes of current application as well as with shorting circuitry attachment conform to the parabolic growth law. The results pertaining to the two different modes of impressed current have been discussed considering both the phenomena of electrolysis of the oxide electrolyte and the polarization at the two phase boundaries. The enhancement and the reduction in rates under uninterrupted impressed current conditions are explained on the basis of increased and decreased average defect concentrations, respectively, within the oxide layer. The acceleration and deceleration in the rates under interrupted mode of current flow have been explained in the light of sustenance of a steeper and flatter electrochemical-potential gradient of defects, respectively, across the growing-oxide layer. The possible different responses of the metal/oxide and oxide/air interfaces to the impressed current brought into play by two different modes of current application, have enabled to display a better insight on the mechanistic aspects of scale growth under the influence of an externally applied current.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 96441
- Journal Information:
- Oxidation of Metals, Vol. 43, Issue 3-4; Other Information: PBD: Apr 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of short-circuiting on the oxidation kinetics of copper and its doped varieties in the temperature range of 523-1073 K
Influence of an externally-applied static charge on the oxidation kinetics of copper