Apparent Yield Strength of Hot-Pressed SiCs
- ORNL
- University of Wisconsin, Platteville
Apparent yield strengths (YApp) of four hot-pressed silicon carbides (SiC-B, SiC-N,SiC-HPN, and SiC-SC-1RN) were estimated using diamond spherical or Hertzian indentation. The von Mises and Tresca criteria were considered. The developed test method was robust, simple and quick to execute, and thusly enabled the acquisition of confident sampling statistics. The choice of indenter size, test method, and method of analysis are described. The compressive force necessary to initiate apparent yielding was identified postmortem using differential interference contrast (or Nomarski) imaging with an optical microscope. It was found that the YApp of SiC-HPN (14.0 GPa) was approximately 10% higher than the equivalently valued YApp of SiC-B, SiC-N, and SiC-SC-1RN. This discrimination in YApp shows that the use of this test method could be insightful because there were no differences among the average Knoop hardnesses of the four SiC grades.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- Work for Others (WFO)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 958850
- Resource Relation:
- Conference: 32nd International Conference & Exposition on Advanced Ceramics and Composites, Daytona Beach, FL, USA, 20080127, 20080201
- Country of Publication:
- United States
- Language:
- English
Similar Records
Knoop Hardness - Apparent Yield Stress Relationship in Ceramics
SPHERICAL INDENTATION OF SiC