The enthalpy of occlusion of the LiC1-KC1 eutectic salt in zeolite 4A.
The molar enthalpy of occlusion of the (lithium chloride + potassium chloride) eutectic salt in zeolite 4A at the salt melting temperature {Delta}{sub 9cc}H{sub m}(T{sub fus}) was measured using differential scanning calorimetry. It was found that up to a mole fraction of the salt x = 0.931 in the (salt + zeolite) mixture, which is near the expected zeolite occlusion limit, {Delta}{sub occ}H{sub m}(T{sub fus}) was negative and directly proportional to x . Thus, within this composition range, the partial molar enthalpy of occlusion of the (lithium chloride + potassium chloride) eutectic salt in zeolite 4A at the salt melting temperature is constant and equal to - (24 {+-}1)kJ {center_dot} mol{sup -1}.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- NE
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 942449
- Report Number(s):
- ANL/CMT/JA-31572; JCTDAF; TRN: US200916%%477
- Journal Information:
- J. Chem. Thermodyn., Vol. 31, Issue 6 ; Jun. 1999; ISSN 0021-9614
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Adsorption of eutectic LiCl-KCl into zeolite 4A using a mechanically fluidized vacuum system
Occlusion and ion exchange in the molten (lithium chloride + potassium chloride + alkaline earth chloride) salt + zeolite 4A system with alkaline earth chlorides of calcium and strontium, and in the molten (lithium chloride + potassium chloride + actinide chloride) salt + zeolite 4A system with the actinide chloride of uranium.
Occlusion and ion exchange in the molten (lithium chloride-potassium chloride-alkali metal chloride) salt + zeolite 4A system with alkali metal chlorides of sodium, rubidium, and cesium.
Journal Article
·
Tue Jun 01 00:00:00 EDT 1999
· Industrial and Engineering Chemistry Research
·
OSTI ID:942449
Occlusion and ion exchange in the molten (lithium chloride + potassium chloride + alkaline earth chloride) salt + zeolite 4A system with alkaline earth chlorides of calcium and strontium, and in the molten (lithium chloride + potassium chloride + actinide chloride) salt + zeolite 4A system with the actinide chloride of uranium.
Journal Article
·
Tue Apr 01 00:00:00 EST 2003
· Metall. Mater. Trans. B
·
OSTI ID:942449
Occlusion and ion exchange in the molten (lithium chloride-potassium chloride-alkali metal chloride) salt + zeolite 4A system with alkali metal chlorides of sodium, rubidium, and cesium.
Journal Article
·
Fri Jun 01 00:00:00 EDT 2001
· Metall. Mater. Trans. B
·
OSTI ID:942449