Oxidation of zirconium alloys in 2.5 kPa water vapor for tritium readiness.
A more reactive liner material is needed for use as liner and cruciform material in tritium producing burnable absorber rods (TPBAR) in commercial light water nuclear reactors (CLWR). The function of these components is to convert any water that is released from the Li-6 enriched lithium aluminate breeder material to oxide and hydrogen that can be gettered, thus minimizing the permeation of tritium into the reactor coolant. Fourteen zirconium alloys were exposed to 2.5 kPa water vapor in a helium stream at 300 C over a period of up to 35 days. Experimental alloys with aluminum, yttrium, vanadium, titanium, and scandium, some of which also included ternaries with nickel, were included along with a high nitrogen impurity alloy and the commercial alloy Zircaloy-2. They displayed a reactivity range of almost 500, with Zircaloy-2 being the least reactive.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 942209
- Report Number(s):
- SAND2008-2638; TRN: US0900419
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fundamental Studies of Tritium Formation and Diffusivity in Pure and Defective Zircaloy-4 Getters
Fundamental Studies of Tritium Diffusivity and Formation on the Surfaces of Defective LiAlO2 Pellets