Biocompatible core-shell magnetic nanoparticles for cancer treatment
Non-toxic magnetic nanoparticles (MNPs) have expanded the treatment delivery options in the medical world. With a size range from 2 to 200 nm MNPs can be compiled with most of the small cells and tissues in living body. Monodispersive iron-iron oxide core shell nanoparticles were prepared in our novel cluster deposition system. This unique method of preparing the core shell MNPs gives nanoparticles very high magnetic moment. We tested the nontoxicity and uptake of MNPs coated with/without dextrin by incubating them with rat LX-1 small cell lung cancer cells (SCLC). Since core iron enhances the heating effect [7] the rate of oxidation of iron nanoparticles was tested in deionized water at certain time interval. Both coated and noncoated MNPs were successfully uptaken by the cells, indicating that the nanoparticles were not toxic. The stability of MNPs was verified by X-ray diffraction (XRD) scan after 0, 24, 48, 96, 204 hours. Due to the high magnetic moment offered by MNPs produced in our lab, we predict that even in low applied external alternating field desired temperature can be reached in cancer cells in comparison to the commercially available nanoparticles. Moreover, our MNPs do not require additional anti-coagulating agents and provide a cost effective means of treatment with significantly lower dosage in the body in comparison to commercially available nanoparticles.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States). Environmental Molecular Sciences Lab. (EMSL)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 934884
- Report Number(s):
- PNNL-SA-57437; JAPIAU; 2573; 2573a; KC0303020; TRN: US200814%%551
- Journal Information:
- Journal of Applied Physics, 103(7):Art. No.07A308, Vol. 103, Issue 7; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Efficient internalization of silica-coated iron oxide nanoparticles of different sizes by primary human macrophages and dendritic cells
Spin canting across core/shell Fe3O4/MnxFe3–xO4 nanoparticles