NOx uptake on alkaline earth oxides (BaO, MgO, CaO and SrO) supported on γ-Al2O3
NOx uptake experiments were performed on a series of alkaline earth oxide (AEO) (MgO, CaO, SrO, BaO) on γ-alumina materials. Temperature Programmed Desorption (TPD) conducted on He flow revealed the presence of two kinds of nitrate species: i.e. bulk and surface nitrates. The ratio of these two types of nitrate species strongly depends on the nature of the alkaline earth oxide. The amount of bulk nitrate species increases with the basicity of the alkaline earth oxide. This conclusion was supported by the results of infrared and 15N solid state NMR studies of NO2 adsorption. Due to the low melting point of the precursor used for the preparation of MgO/Al2O3 material (Mg(NO3)2), a significant amount of Mg was lost during sample activation (high temperature annealing) resulting in a material with properties were very similar to that of the γ-Al2O3 support. The effect of water on the NOx species formed in the exposure of the AEO-s to NO2 was also investigated. In agreement with our previous findings for the BaO/γ-Al2O3 system, an increase of the bulk nitrate species and the simultaneous decrease of the surface nitrate phase were observed for all of these materials.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States). Environmental Molecular Sciences Lab. (EMSL)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 929738
- Report Number(s):
- PNNL-SA-57211; CATTEA; 19800; VT0401000; TRN: US200812%%622
- Journal Information:
- Catalysis Today, 136(1-2):121-127, Vol. 136, Issue 1-2; ISSN 0920-5861
- Country of Publication:
- United States
- Language:
- English
Similar Records
Water-induced morphology changes in BaO/γ-Al2O3 NOx storage materials: an FTIR, TPD, and time-resolved synchrotron XRD study
NOx Uptake Mechanism on Pt/BaO/Al2O3 Catalysts