MEASUREMENT OF THE HIGH-FIELD Q-DROP IN A LARGE-GRAIN NIOBIUM CAVITY FOR DIFFERENT OXIDATION PROCESSES

Conference · Wed Jan 23 00:00:00 EST 2008

OSTI ID:922264

Ciovati, Gianluigi; Kneisel, Peter; Gurevich, Alex

In this contribution, we present the results from a series of RF tests at 1.7 K and 2.0 K on a single-cell cavity made of high-purity large (with area of the order of few cm2) grain niobium which underwent various oxidation processes. After initial buffered chemical polishing, anodization, baking in pure oxygen atmosphere and baking in air up to 180 °C was applied with the objective of clearly identifying the role of oxygen and the oxide layer on the Q-drop. During each rf test a temperature mapping system was used allowing to measure the local temperature rise of the cavity outer surface due to RF losses, which gives information about the losses location, their field dependence and space distribution on the RF surface. The results confirmed that the depth affected by baking is about 20 – 30 nm from the surface and showed that the Q-drop did not re-appear in a previously baked cavity by further baking at 120 °C in pure oxygen atmosphere or in air up to 180 °C. A statistic of the position of the “hot-spots” on the cavity surface showed that grain-boundaries are not the preferred location. An interesting correlation was found between the Q-drop onset, the quench field and the low-field energy gap, which supports the hypothesis of thermo-magnetic instability governing the Q-drop and the baking effect.

• Research Organization: Thomas Jefferson National Accelerator Facility (TJNAF), Newport News, VA (United States)
• Sponsoring Organization: USDOE Office of Science (SC)
• DOE Contract Number: AC05-06OR23177
• OSTI ID: 922264
• Report Number(s): JLAB-ACC-07-775; DOE/OR/23177-0283
• Resource Relation: Conference: 13th Workshop on RF Superconductivity, Beijing, China, Oct. 14 - 19, 2007
• Country of Publication: United States
• Language: English