The Corrosion Resistance of Fe-Based Amorphous Metals: Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4 and Other Compositions
Several Fe-based amorphous metals were developed with good corrosion resistance. These materials have been produced as melt-spun ribbons, ingots, and thermal-spray coatings. Cyclic polarization has been conducted in several aggressive environments, at ambient temperature, as well as temperatures approaching the boiling points of the test solutions. The hypothesis that the corrosion resistance of iron-based amorphous metals can be enhanced through application of heuristic principles related to the additions of chromium, molybdenum, tungsten has been tested and found to have merit. Chromium (Cr), molybdenum (Mo) and tungsten (W) provide corrosion resistance; boron (B) enables glass formation; and rare earths such as yttrium (Y) lower critical cooling rate (CCR). The high boron content of this particular amorphous metal makes this amorphous alloy an effective neutron absorber, and suitable for criticality control applications. In general, the corrosion resistance of such iron-based amorphous metals is maintained at operating temperatures up to the glass transition temperature.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 920869
- Report Number(s):
- UCRL-CONF-232607; TRN: US200805%%219
- Resource Relation:
- Conference: Presented at: Materials Science & Technology 2007 Conference and Exhibition, Detroit, MI, United States, Sep 16 - Sep 20, 2007
- Country of Publication:
- United States
- Language:
- English
Similar Records
Quantification of corrosion resistance of a new-class of criticality control materials: thermal-spray coatings of high-boron iron-based amorphous metals - Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4
Electrochemical Studies of Passive Film Stability on Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4 Amorphous Metal in Seawater at 90oCElectrochemical Studies of Passive Film Stability on Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4 Amorphous Metal in Seawater at 9