Development Of A Novel Catalyst For No Decomposition
Abstract
Air pollution arising from the emission of nitrogen oxides as a result of combustion taking place in boilers, furnaces and engines, has increasingly been recognized as a problem. New methods to remove NO{sub x} emissions significantly and economically must be developed. The current technology for post-combustion removal of NO is the selective catalytic reduction (SCR) of NO by ammonia or possibly by a hydrocarbon such as methane. The catalytic decomposition of NO to give N2 will be preferable to the SCR process because it will eliminate the costs and operating problems associated with the use of an external reducing species. The most promising decomposition catalysts are transition metal (especially copper)-exchanged zeolites, perovskites, and noble metals supported on metal oxides such as alumina, silica, and ceria. The main shortcoming of the noble metal reducible oxide (NMRO) catalysts is that they are prone to deactivation by oxygen. It has been reported that catalysts containing tin oxide show oxygen adsorption behavior that may involve hydroxyl groups attached to the tin oxide. This is different than that observed with other noble metal-metal oxide combinations, which have the oxygen adsorbing on the noble metal and subsequently spilling over to the metal oxide. This observation leadsmore »
- Authors:
- Publication Date:
- Research Org.:
- Hampton Univ., Hampton, VA (United States)
- Sponsoring Org.:
- USDOE
- OSTI Identifier:
- 896871
- DOE Contract Number:
- FG26-03NT41911
- Resource Type:
- Technical Report
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 54 ENVIRONMENTAL SCIENCES; ACTIVATION ENERGY; AIR POLLUTION; CATALYSTS; DEACTIVATION; MASS TRANSFER; NITROGEN OXIDES; OXYGEN; POWER PLANTS; SELECTIVE CATALYTIC REDUCTION; TIN OXIDES; WATER VAPOR
Citation Formats
Akyurtlu, Ates, and Akyurtlu, Jale F. Development Of A Novel Catalyst For No Decomposition. United States: N. p., 2006.
Web. doi:10.2172/896871.
Akyurtlu, Ates, & Akyurtlu, Jale F. Development Of A Novel Catalyst For No Decomposition. United States. https://doi.org/10.2172/896871
Akyurtlu, Ates, and Akyurtlu, Jale F. 2006.
"Development Of A Novel Catalyst For No Decomposition". United States. https://doi.org/10.2172/896871. https://www.osti.gov/servlets/purl/896871.
@article{osti_896871,
title = {Development Of A Novel Catalyst For No Decomposition},
author = {Akyurtlu, Ates and Akyurtlu, Jale F},
abstractNote = {Air pollution arising from the emission of nitrogen oxides as a result of combustion taking place in boilers, furnaces and engines, has increasingly been recognized as a problem. New methods to remove NO{sub x} emissions significantly and economically must be developed. The current technology for post-combustion removal of NO is the selective catalytic reduction (SCR) of NO by ammonia or possibly by a hydrocarbon such as methane. The catalytic decomposition of NO to give N2 will be preferable to the SCR process because it will eliminate the costs and operating problems associated with the use of an external reducing species. The most promising decomposition catalysts are transition metal (especially copper)-exchanged zeolites, perovskites, and noble metals supported on metal oxides such as alumina, silica, and ceria. The main shortcoming of the noble metal reducible oxide (NMRO) catalysts is that they are prone to deactivation by oxygen. It has been reported that catalysts containing tin oxide show oxygen adsorption behavior that may involve hydroxyl groups attached to the tin oxide. This is different than that observed with other noble metal-metal oxide combinations, which have the oxygen adsorbing on the noble metal and subsequently spilling over to the metal oxide. This observation leads one to believe that the Pt/SnO{sub 2} catalysts may have a potential as NO decomposition catalysts in the presence of oxygen. This prediction is also supported by some preliminary data obtained for NO decomposition on a Pt/SnO2 catalyst in the PI's laboratory. The main objective of the research that is being undertaken is the evaluation of the Pt/SnO2 catalysts for the decomposition of NO in simulated power plant stack gases with particular attention to the resistance to deactivation by O{sub 2}, CO{sub 2}, and elevated temperatures. Temperature programmed desorption (TPD) and temperature programmed reaction (TPRx) studies on Pt/SnO2 catalysts having different noble metal concentrations and pretreated under different conditions were done. It is also planned to perform NO decomposition tests in a laboratory-size packed-bed reactor to obtain long-term deactivation data. In the previous reporting periods, runs were made with catalysts containing 15% Pt and 10% Pt on SnO{sub 2} were done. Catalysts containing 10% Pt resulted in significantly lower activities than 15% PT catalysts. Therefore, in the following tests 15% Pt/SnO{sub 2} catalysts were used. In the current reporting period runs to elucidate the effects of temperature, oxygen, water vapor, pretreatment temperature, and space velocity on NO dissociation were completed. It was found that the presence of oxygen and water vapor did not affect the activation energy of the NO dissociation reaction indicating the presence of the same rate controlling step for all feed compositions. Activation energy was higher for higher gas velocities suggesting the presence of mass transfer limitations at lower velocities. Presence of oxygen in the feed inhibited the NO decomposition. Having water vapor in the feed did not significantly affect the catalyst activity for catalysts pretreated at 373 K, but significantly reduced catalyst activity for catalysts pretreated at 900 K.},
doi = {10.2172/896871},
url = {https://www.osti.gov/biblio/896871},
journal = {},
number = ,
volume = ,
place = {United States},
year = {Thu Sep 14 00:00:00 EDT 2006},
month = {Thu Sep 14 00:00:00 EDT 2006}
}