Silicon Carbide Micro-devices for Combustion Gas Sensing under Harsh Conditions
A sensor based on the wide bandgap semiconductor, silicon carbide (SiC), has been developed for the detection of combustion products in power plant environments. The sensor is a catalytic gate field effect device that can detect hydrogen-containing species in chemically reactive, high temperature environments. For fast and stable sensor response measurements, a gate activation process is required. Activation of all sensors took place by switching back and forth between oxidizing (1.0% oxygen in nitrogen) and reducing (10% hydrogen in nitrogen) gases for several hours at a sensor temperature {ge}620 C. All 52 devices on the sensor chip were activated simultaneously by flooding the entire chip with gas. The effects of activation on surface morphology and structure of Pt gates before and after activation were investigated. The optical images obtained from Pt gates demonstrated a clear transition from a smooth and shiny surface to a grainy and cloudy surface morphology. XRD scans collected from Pt gates suggest the presence of an amorphous layer and species other than Pt (111) after activation. The reliability of the gate insulator of our metal-oxide-SiC sensors for long-term device operation at 630 C was studied. We find that the dielectric is stable against breakdown due to electron injection from the substrate with gate leakage current densities as low at 5nA/cm{sup 2} at 630 C. We also designed and constructed a new nano-reactor capable of high gas flow rates at elevated pressure. Our reactor, which is a miniature version of an industrial reactor, is designed to heat the flowing gas up to 700 C. Measurements in ultrahigh vacuum demonstrated that hydrogen sulfide readily deposits sulfur on the gate surface, even at the very high hydrogen/hydrogen sulfide ratios (10{sup 3}-10{sup 5}) expected in applications. Once deposited, the sulfur adversely affects sensor response, and could not be removed by exposure to hydrogen at the temperatures and pressures accessible in the ultrahigh vacuum experiments. Oxygen exposures, however, were very effective at removing sulfur, and the device performance after sulfur removal was indistinguishable from performance before exposure to H{sub 2}S.
- Research Organization:
- Michigan State Univ., East Lansing, MI (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- FC26-03NT41847
- OSTI ID:
- 882583
- Country of Publication:
- United States
- Language:
- English
Similar Records
SILICON CARBIDE MICRO-DEVICES FOR COMBUSTION GAS SENSING UNDER HARSH CONDITIONS
Annual Report: Fuels (30 September 2012)