Glass capable of ionic conduction and method of preparation
Patent
·
OSTI ID:865596
- Park Forest, IL
- Jerusalem, IL
- Fort Collins, CO
- Downers Grove, IL
Sulfide glasses capable of conducting alkali metal ions are prepared from a nonmetal glass former such as GeS.sub.2, B.sub.2 S.sub.3 and SiS.sub.2 in mixture with a glass modifier such as Na.sub.2 S or another alkali metal sulfide. A molten mixture of the constituents is rapidly quenched to below the glass transition temperature by contact with a metal mold. The rapid quench is sufficient to prevent crystallization and permit solidification as an amorphous solid mixture. An oxygen-free atmosphere is maintained over the mixture to prevent oxidation. A new glass system of (1-X) Na.sub.2 O:XB.sub.2 S.sub.3 is disclosed.
- Research Organization:
- Argonne National Laboratory (ANL), Argonne, IL (United States)
- DOE Contract Number:
- W-31109-ENG-38
- Assignee:
- United States of America as represented by United States (Washington, DC)
- Patent Number(s):
- US 4542108
- OSTI ID:
- 865596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Glass capable of ionic conduction and method of preparation
Glass capable of ionic conduction and method of preparation
Glass capable of ionic conduction and method of preparation
Patent
·
Sun Jan 01 00:00:00 EST 1984
·
OSTI ID:865596
+1 more
Glass capable of ionic conduction and method of preparation
Patent
·
Tue Sep 17 00:00:00 EDT 1985
·
OSTI ID:865596
+1 more
Glass capable of ionic conduction and method of preparation
Patent
·
Tue Feb 21 00:00:00 EST 1984
·
OSTI ID:865596
+1 more
Related Subjects
glass
capable
ionic
conduction
method
preparation
sulfide
glasses
conducting
alkali
metal
prepared
nonmetal
former
sis
mixture
modifier
na
molten
constituents
rapidly
quenched
below
transition
temperature
contact
mold
rapid
quench
sufficient
prevent
crystallization
permit
solidification
amorphous
solid
oxygen-free
atmosphere
maintained
oxidation
1-x
xb
disclosed
rapidly quenched
glass former
metal sulfide
alkali metal
transition temperature
solid mixture
glass transition
oxygen-free atmosphere
molten mixture
prevent oxidation
prevent crystallization
rapid quench
nonmetal glass
ionic conduction
sulfide glasses
glass modifier
glasses capable
glass capable
free atmosphere
metal glass
amorphous solid
conducting alkali
/501/65/252/429/
capable
ionic
conduction
method
preparation
sulfide
glasses
conducting
alkali
metal
prepared
nonmetal
former
sis
mixture
modifier
na
molten
constituents
rapidly
quenched
below
transition
temperature
contact
mold
rapid
quench
sufficient
prevent
crystallization
permit
solidification
amorphous
solid
oxygen-free
atmosphere
maintained
oxidation
1-x
xb
disclosed
rapidly quenched
glass former
metal sulfide
alkali metal
transition temperature
solid mixture
glass transition
oxygen-free atmosphere
molten mixture
prevent oxidation
prevent crystallization
rapid quench
nonmetal glass
ionic conduction
sulfide glasses
glass modifier
glasses capable
glass capable
free atmosphere
metal glass
amorphous solid
conducting alkali
/501/65/252/429/