High surface area ThO.sub.2 catalyst and method of preparing it
Patent
·
OSTI ID:865536
- Alamo, CA
- Berkeley, CA
- Walnut Creek, CA
A ThO.sub.2 catalyst having a high surface area of about 80-125 m.sup.2 /g is synthesized. The compound is synthesized by simultaneously mixing an aqueous solution of ThNO.sub.3 (NO.sub.3).sub.4.4H.sub.2 O with an aqueous solution of Na.sub.2 CO.sub.3.H.sub.2 O, to produce a solution and solid ThOCO.sub.3. The solid ThOCO.sub.3 is separated from the solution, and then calcined at a temperature of about 225.degree.-300.degree. C. for about 40-55 hours to produce ThO.sub.2. The ThO.sub.2 catalyst produced includes Na present as a substitutional cation in an amount equal to about 5-10 atom percent.
- Research Organization:
- Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States)
- DOE Contract Number:
- W-7405-ENG-48
- Assignee:
- United States of America as represented by United States (Washington, DC)
- Patent Number(s):
- US 4532230
- OSTI ID:
- 865536
- Country of Publication:
- United States
- Language:
- English
Similar Records
High surface area THO/sub 2/ catalyst and method of preparing it
High surface area ThO/sub 2/ catalyst
Highly-basic large-pore zeolite catalysts for NOx reduction at low temperatures
Patent
·
Tue Jul 30 00:00:00 EDT 1985
·
OSTI ID:865536
High surface area ThO/sub 2/ catalyst
Patent
·
Tue Jun 21 00:00:00 EDT 1983
·
OSTI ID:865536
Highly-basic large-pore zeolite catalysts for NOx reduction at low temperatures
Patent
·
Tue Feb 03 00:00:00 EST 2004
·
OSTI ID:865536
+1 more
Related Subjects
surface
catalyst
method
preparing
80-125
synthesized
compound
simultaneously
mixing
aqueous
solution
thno
4h
na
produce
solid
thoco
separated
calcined
temperature
225
degree
-300
40-55
hours
produced
substitutional
cation
amount
equal
5-10
atom
percent
amount equal
atom percent
aqueous solution
simultaneously mix
/502/423/
catalyst
method
preparing
80-125
synthesized
compound
simultaneously
mixing
aqueous
solution
thno
4h
na
produce
solid
thoco
separated
calcined
temperature
225
degree
-300
40-55
hours
produced
substitutional
cation
amount
equal
5-10
atom
percent
amount equal
atom percent
aqueous solution
simultaneously mix
/502/423/