INVESTIGATION OF NOVEL ALLOY TiC-Ni-Ni3Al FOR SOLID OXIDE FUEL CELL INTERCONNECT APPLICATIONS
Solid oxide fuel cell interconnect materials must meet stringent requirements. Such interconnects must operate at temperatures approaching 800 C while resisting oxidation and reduction, which can occur from the anode and cathode materials and the operating environment. They also must retain their electrical conductivity under these conditions and possess compatible coefficients of thermal expansion as the anode and cathode. Results are presented in this report for fuel cell interconnect candidate materials currently under investigation based upon nano-size titanium carbide (TiC) powders. The TiC is liquid phase sintered with either nickel (Ni) or nickel-aluminide (Ni{sub 3}Al) in varying concentrations. The oxidation resistance of the submicron grain TiC-metal materials is presented as a function weight change versus time at 700 C and 800 C for varying content of metal/intermetallic in the system. Electrical conductivity at 800 C as a function of time is also presented for TiC-Ni to demonstrate the vitality of these materials for interconnect applications. TGA studies showed that the weight gain was 0.8 mg/cm{sup 2} for TiC(30)-Ni(30wt.%) after 100 hours in wet air at 800 C and the weight gain was calculated to be 0.5205 mg/cm{sup 2} for TiC(30)- Ni(10 wt.%) after 100 hours at 700 C and 100 hours at 800 C. At room temperature the electrical conductivity was measured to be 2444 1/[ohm.cm] for TiC-Ni compositions. The electrical conductivities at 800 C in air was recorded to be 19 1/[ohm.cm] after 125 hours. Two identical samples were supplied to PNNL (Dr. Jeff Stevenson) for ASR testing during the pre-decision period and currently they are being tested there. Fabrication, oxidation resistance and electrical conductivity studies indicate that TiC-Ni-Ni{sub 3}Al ternary appears to be a very important system for the development of interconnect composition for solid oxide fuel cells.
- Research Organization:
- Southern Illinois University at Carbondale (US)
- Sponsoring Organization:
- (US)
- DOE Contract Number:
- FC26-04NT42224
- OSTI ID:
- 839127
- Resource Relation:
- Other Information: PBD: 25 Jan 2005
- Country of Publication:
- United States
- Language:
- English
Similar Records
Durable, Impermeable Brazes for Solid Oxide Fuel Cells (Final Report)
Improving intermediate temperature performance of Ni-YSZ cermet anodes for solid oxide fuel cells by liquid infiltration of nickel nanoparticles