Surface preparation and characterization of the icosahedral Al-Pd-Mn-Ga quasicrystal
Journal Article
·
· Journal of Alloys and Compounds
Auger electron spectroscopy and low-energy electron diffraction (LEED) provide basic information about the structure and composition of the fivefold surface of the quaternary quasicrystal, icosahedral Al67Pd4Mn21Ga8. Surface preparation techniques established previously for two of the icosahedral ternary alloys, Al-Pd-Mn and Al-Cu-Fe, appear to be similarly effective for Al-Pd-Mn-Ga. After annealing in the range 600-950 K, the surface concentration of Ga is constant and low. After annealing in the range 900-950 K, a good LEED pattern is obtained. LEED indicates that Ga changes the surface structure significantly.
- Research Organization:
- Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
- Sponsoring Organization:
- USDOE Director, Office of Science. Office of Basic Energy Sciences. Division of Materials Sciences (US)
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 837803
- Report Number(s):
- LBNL-49729; R&D Project: 505501; TRN: US200506%%465
- Journal Information:
- Journal of Alloys and Compounds, Vol. 338, Issue 1-2; Other Information: Submitted to Journal of Alloys and Compounds: Volume 338, No.1-2; Journal Publication Date: 05/16/2002; PBD: 8 Jan 2002
- Country of Publication:
- United States
- Language:
- English
Similar Records
Scanning tuneeling microscopy studies of fivefold surfaces of icosahedral Al-Pd-Mn quasicrystals and of thin silver films on those surfaces
Surface structures of Al-Pd-Mn and Al-Cu-Fe icosahedral quasicrystals
Copper adsorption on the fivefold Al{sub 70}Pd{sub 21}Mn{sub 9} quasicrystal surface
Thesis/Dissertation
·
Tue Jan 01 00:00:00 EST 2008
·
OSTI ID:837803
Surface structures of Al-Pd-Mn and Al-Cu-Fe icosahedral quasicrystals
Thesis/Dissertation
·
Fri Feb 12 00:00:00 EST 1999
·
OSTI ID:837803
Copper adsorption on the fivefold Al{sub 70}Pd{sub 21}Mn{sub 9} quasicrystal surface
Journal Article
·
Fri Jul 15 00:00:00 EDT 2005
· Physical Review. B, Condensed Matter and Materials Physics
·
OSTI ID:837803
+6 more