Studies of components for thermally regenerative electrochemical systems. Final report, 1 August 1985-31 December 1987
Technical Report
·
OSTI ID:7187951
Electrochemical studies on the reduction of AlCl 4- ion and the anodization of Al(O) in basic 1-methyl-3-ethylimidazolium chloride (ImCl) mixed with aluminum chloride (AlCl3) were carried out; a basic melt is one containing excess ImCl. It was not found possible to reduce the AlCl4 ion at temperatures as high as 250 deg C. The anodization of aluminum was found to be controlled by the diffusion of chloride ion to the electrode. The disposition of Li and Bi were studied at tungsten microelectrodes in LiCl-KCl eutectic molten salt at 450 deg C. Molten salts; ambient temperature chloroaluminates; lithium chloride - potassium chloride eutectic; electrochemistry.
- Research Organization:
- State Univ. of New York, Buffalo, NY (United States). Dept. of Chemistry
- OSTI ID:
- 7187951
- Report Number(s):
- AD-A-256124/9/XAB; CNN: N00014-85-K-0789
- Country of Publication:
- United States
- Language:
- English
Similar Records
Aluminum anodization in a basic ambient temperature molten salt
Wetting behavior of dialkylimidazolium chloroaluminate, a room-temperature molten salt. Interim report, May-September 1984
Electrochemical studies of Lewis acid-base systems for use in thermally regenerable fuel cells. Final report, 30 Apr 89-31 Dec 91
Journal Article
·
Mon May 01 00:00:00 EDT 1989
· Journal of the Electrochemical Society; (USA)
·
OSTI ID:7187951
Wetting behavior of dialkylimidazolium chloroaluminate, a room-temperature molten salt. Interim report, May-September 1984
Technical Report
·
Thu Aug 01 00:00:00 EDT 1985
·
OSTI ID:7187951
Electrochemical studies of Lewis acid-base systems for use in thermally regenerable fuel cells. Final report, 30 Apr 89-31 Dec 91
Technical Report
·
Wed Feb 12 00:00:00 EST 1992
·
OSTI ID:7187951
Related Subjects
36 MATERIALS SCIENCE
ALUMINIUM
ANODIZATION
ALUMINIUM CHLORIDES
ELECTROCHEMISTRY
AMBIENT TEMPERATURE
ANIONS
ANODES
BENCH-SCALE EXPERIMENTS
BISMUTH
CATHODES
CATIONS
CHEMICAL ANALYSIS
CHLORIDES
DATA-FLOW PROCESSING
DIFFUSION
ELECTRODES
ELECTROLYTES
EUTECTICS
IMIDAZOLES
ION SELECTIVE ELECTRODE ANALYSIS
LITHIUM
LITHIUM CHLORIDES
MOLTEN SALTS
POTASSIUM
POTASSIUM CHLORIDES
REDUCTION
RESEARCH PROGRAMS
TUNGSTEN
ALKALI METAL COMPOUNDS
ALKALI METALS
ALUMINIUM COMPOUNDS
AZOLES
CHARGED PARTICLES
CHEMICAL COATING
CHEMICAL REACTIONS
CHEMISTRY
CHLORINE COMPOUNDS
CORROSION PROTECTION
DEPOSITION
ELECTROCHEMICAL COATING
ELECTROLYSIS
ELEMENTS
HALIDES
HALOGEN COMPOUNDS
HETEROCYCLIC COMPOUNDS
IONS
LITHIUM COMPOUNDS
LITHIUM HALIDES
LYSIS
METALS
ORGANIC COMPOUNDS
ORGANIC NITROGEN COMPOUNDS
POTASSIUM COMPOUNDS
PROGRAMMING
SALTS
SURFACE COATING
TRANSITION ELEMENTS
360102* - Metals & Alloys- Structure & Phase Studies
ALUMINIUM
ANODIZATION
ALUMINIUM CHLORIDES
ELECTROCHEMISTRY
AMBIENT TEMPERATURE
ANIONS
ANODES
BENCH-SCALE EXPERIMENTS
BISMUTH
CATHODES
CATIONS
CHEMICAL ANALYSIS
CHLORIDES
DATA-FLOW PROCESSING
DIFFUSION
ELECTRODES
ELECTROLYTES
EUTECTICS
IMIDAZOLES
ION SELECTIVE ELECTRODE ANALYSIS
LITHIUM
LITHIUM CHLORIDES
MOLTEN SALTS
POTASSIUM
POTASSIUM CHLORIDES
REDUCTION
RESEARCH PROGRAMS
TUNGSTEN
ALKALI METAL COMPOUNDS
ALKALI METALS
ALUMINIUM COMPOUNDS
AZOLES
CHARGED PARTICLES
CHEMICAL COATING
CHEMICAL REACTIONS
CHEMISTRY
CHLORINE COMPOUNDS
CORROSION PROTECTION
DEPOSITION
ELECTROCHEMICAL COATING
ELECTROLYSIS
ELEMENTS
HALIDES
HALOGEN COMPOUNDS
HETEROCYCLIC COMPOUNDS
IONS
LITHIUM COMPOUNDS
LITHIUM HALIDES
LYSIS
METALS
ORGANIC COMPOUNDS
ORGANIC NITROGEN COMPOUNDS
POTASSIUM COMPOUNDS
PROGRAMMING
SALTS
SURFACE COATING
TRANSITION ELEMENTS
360102* - Metals & Alloys- Structure & Phase Studies