Formation of high angle grain boundaries during the deformation of aluminum single crystals
Journal Article
·
· Scr. Metall.; (United States)
Large local misorientations arise due to the sequence of slip systems which are active in a given region during deformation. 17 refs.
- Research Organization:
- McMaster Univ, Hamilton, Ontario, Canada
- OSTI ID:
- 6950637
- Journal Information:
- Scr. Metall.; (United States), Vol. 16:5
- Country of Publication:
- United States
- Language:
- English
Similar Records
Studies of grain boundary regions in deformed polycrystalline aluminum using spherical nanoindentation
Deformation Mechanisms at Grain Boundaries in Polycrystals (Final Report)
Characterization of microstructures near grain boundary in hot deformed AA 3104 aluminum alloy
Journal Article
·
Mon Feb 01 00:00:00 EST 2016
· International Journal of Plasticity
·
OSTI ID:6950637
Deformation Mechanisms at Grain Boundaries in Polycrystals (Final Report)
Technical Report
·
Tue Dec 10 00:00:00 EST 2019
·
OSTI ID:6950637
+1 more
Characterization of microstructures near grain boundary in hot deformed AA 3104 aluminum alloy
Journal Article
·
Sat Jan 15 00:00:00 EST 2011
· Materials Characterization
·
OSTI ID:6950637